| Judul Artikel | PELEPASAN ION KROMIUM (Cr) PADA KAWAT STAINLESS STEEL AUSTENITE 304 DAN AUSTRALIAN DALAM AIR KALSIUM HIPOKLORIT (Ca(ClO)2) |
|---|
| Abstrak (Bhs. Indonesia) | Austenite 304 dan stainless steel Australian. Stainless steel memiliki sifat terhadap korosi karena adanya peran kromium. Stainless steel Austenite 304 dan stainless steel Australian memiliki perbedaan pada banyaknya kandungan karbon yang dimiliki. Karbon pada stainless steel berfungsi sebagai pemberi sifat kekerasan pada logam. Perbedaan jumlah komposisi karbon menyebabkan ketahanan korosi kedua jenis kawat tersebut berbeda. Pelepasan ion kromium pada stainless steel dapat disebabkan oleh kondisi saat melakukan aktivitas renang di kolam renang yang mengandung kalsium hipoklorit (Ca(ClO)2). Kalsium hipoklorit (Ca(ClO)2) merupakan media elektrolit yang dapat melepaskan ion Cr3+ dari ikatannya. Penelitian ini bertujuan untuk mengetahui konsentrasi pelepasan ion kromium kawat stainless steel Austenite 304 dan Australian dalam air kalsium hipoklorit pada hari ke-3, 5, 7, dan 9. Jenis penelitian ini yaitu eksperimental laboratoris dengan 64 sampel sebagai uji konsentrasi pelepasan ion kromium pada kawat stainless steel Austenite 304 dan Australian dengan kelompok perendaman masing-masing kawat yaitu hari ke-3, 5, 7, dan 9. Media perendaman dibuat dengan bubuk kalsium hipoklorit sebanyak 1 g dan aquabides 1 L. Konsentrasi pelepasan ion kromium diukur dengan Atomic Absorbtion Spectrophotometry (AAS). Data dilakukan uji parametrik Independent T-test dan uji One-Way ANOVA. Kedua hasil uji statistik tersebut menunjukkan perbedaan yang signifikan (p<0,05). Kawat stainless steel Austenite 304 memiliki konsentrasi pelepasan ion kromium lebih tinggi dibandingkan dengan stainless steel Australian. Hari ke-9 memiliki konsentrasi pelepasan ion kromium tertinggi pada kedua jenis kawat. |
|---|
| Abtrak (Bhs. Inggris) | Iron, nickel, chromium and carbon are the main compositions of stainless steel Austenite 304 and stainless steel Australian. Stainless steel has properties against corrosion due to the role of chromium. Stainless steel Austenite 304 and stainless steel Australian differ in the amount of carbon they have. Carbon in stainless steel serves as a giver of the hardness of the metal. The difference in the amount of carbon composition causes the corrosion resistance of the two types of wire to be different. The release of chromium ions in stainless steel can be caused by conditions when swimming in swimming pools that contain calcium hypochlorite (Ca(ClO)2). Calcium hypochlorite (Ca(ClO)2) is an electrolyte medium that can release Cr3+ ions from its bonds. This study aims to determine the concentration of chromium ion release of stainless steel Austenite 304 and Australian wire in calcium hypochlorite water on days 3, 5, 7, and 9. The type of this research is experimental laboratory with 64 samples as a test of the concentration of chromium ion release on wire Austenite 304 and Australian stainless steel with immersion groups for each wire, namely day 3, 5, 7, and 9. Immersion media was made with 1 g calcium hypochlorite powder and 1 L. aquabides concentration. The concentration of chromium ion release was measured with Atomic Absorbtion Spectrophotometry (AAS). Data were carried out the Independent T-test parametric test and the One-Way ANOVA test. Both statistical test results showed significant differences (p<0.05). Austenite 304 stainless steel wire has a higher concentration of chromium ion release compared to Australian stainless steel. Day 9 has the highest concentration of chromium ion release in both types of wire. |
|---|
| Kata kunci | kawat ortodonti, stainless steel Austenite 304, stainless steel Australian, kalsium hipoklorit, kromium, karbon |
|---|
| Pembimbing 1 | drg. Setiadi Warata Logamarta, Sp.Ort. |
|---|
| Pembimbing 2 | drg. Dian Noviyanti Agus Imam, M.D.Sc. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2020 |
|---|
| Jumlah Halaman | 22 |
|---|
| Tgl. Entri | 2020-02-14 17:04:45.519262 |
|---|