| Judul Artikel | PERBEDAAN KEKUATAN TARIK PELEKATAN SEMEN RESIN MENGGUNAKAN BONDING GENERASI VIII BERBASIS HEMA DAN NON-HEMA TEKNIK TOTAL-ETCH RESTORASI VENEER INDIREK KOMPOSIT |
| Abstrak (Bhs. Indonesia) | Restorasi veneer indirek merupakan suatu restorasi yang membutuhkan proses pengerjaan di luar mulut untuk memperbaiki gigi yang mengalami kelainan. Veneer indirek membutuhkan semen resin dan bahan bonding untuk melekatkannya pada email gigi. Bahan bonding mampu mempengaruhi pelekatan semen resin terhadap email gigi, salah satu faktor penyebabnya adalah perbedaan monomer berupa monomer HEMA dan non-HEMA. Tujuan dari penelitian ini adalah untuk mengetahui perbedaan kekuatan tarik pelekatan semen resin menggunakan bonding generasi VIII berbasis HEMA dan non-HEMA teknik total-etch restorasi veneer indirek komposit. Jenis penelitian ini merupakan penelitian eksperimental laboratoris berupa posttest-only group design dengan membagi sampel menjadi 2 kelompok. Kelompok I adalah bonding yang berbasis HEMA dan kelompok II adalah bonding berbasis non-HEMA. Pengujian dilakukan menggunakan Universal Testing Machine. Hasil yang diperoleh kemudian diuji dengan uji independent t-Test. Didapatkan perbedaan yang bermakna antara kelompok I dengan kelompok II yang ditandai dengan p=0,048 (p<0,05). Simpulan dari penelitian ini adalah bonding generasi VIII berbasis non-HEMA memiliki kekuatan tarik pelekatan lebih tinggi dibandingkan dengan bonding generasi VIII berbasis HEMA. |
| Abtrak (Bhs. Inggris) | Indirect veneer restoration is a restoration processed outside the mouth to repair tooth that has an abnormality. Indirect veneers require resin cement and bonding agent to attach them to tooth enamel. The bonding agent can effect the attachment of resin cement to tooth enamel. One of the contribution factors of the attachment is the monomer difference in the form of HEMA and non-HEMA monomers. The aim of this study was to determine difference in tensile bond strength of resin cement using total-etch technique of HEMA-based and non-HEMA-based 8th generation bonding agent in indirect composite veneer restoration. This type of research was a laboratory experimental study with posttest-only group design by dividing the samples into 2 groups. Group I was HEMA-based bonding agent and group II was non-HEMA-based bonding agent. Testing was done using Universal Testing Machine. The results obtained were tested by the independent t-Test. There was a significant difference between group I and group II with p value = 0.048 (p <0.05). The conclusion of this study is that non-HEMA-based 8th generation bonding agent has a higher tensile bond strength compared to HEMA-based 8th generation bonding agent. |
| Kata kunci | veneer indirek, semen resin, bonding generasi VIII, HEMA, non- HEMA, kekuatan tarik pelekatan |
| Pembimbing 1 | drg. Rinawati Satrio, M.Si |
| Pembimbing 2 | drg. Irfan Dwiandhono, Sp.KG |
| Pembimbing 3 | |
| Tahun | 2019 |
| Jumlah Halaman | 73 |
| Tgl. Entri | 2019-07-30 07:00:20.378116 |