| Judul Artikel | PEMBUATAN PIEZOELEKTRIK Bi0,5Na0,5TiO3–SrTiO3 DOPING Fe2O3 DENGAN METODE SOLID STATE REACTION DAN KARAKTERISASINYA |
|---|
| Abstrak (Bhs. Indonesia) | Penelitian material piezoelektrik Bi0,5Na0,5TiO3-SrTiO3 Doping Fe2O3 telah dilakukan menggunakan metode solid state reaction untuk menentukan karakteristik material yang terbentuk. Variasi doping Fe2O3 adalah sebesar 0 dan 0,1 dalam % mol. Pengujian dilakukan menggunakan X-Ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS), dan LCR meter. Dari hasil penelitian, didapatkan senyawa Bi0,5Na0,5TiO3-SrTiO3 pada variasi 0 % mol dan senyawa baru berupa FeBi5Ti3O15-Na2Ti3O7-SrTiO3 pada variasi 1% mol. Variasi konsentrasi tersebut juga menghasilkan ukuran partikel yang bervariasi, yaitu antara 0,88 µm – 8,23 µm. Konstanta dielektrik (ɛr) yang didapatkan berturut-turut 7.214 dan 12.029 pada temperatur Curie (Tc) 300 ºC dengan impedansi bahan (Z) 136 kΩ dan 137 kΩ. |
|---|
| Abtrak (Bhs. Inggris) | Research on piezoelectric material Bi0,5Na0,5TiO3-SrTiO3 Doping Fe2O3 has been carried out using the solid state reaction method to determine the characteristics of the material formed. The variation of Fe2O3 doping is 0 and 0.1 in mol%. Tests were carried out using X-Ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS), and LCR meters. From the results of the study, the compounds Bi0,5Na0,5TiO3-SrTiO3 obtained at variations of 0 mol % and new compounds in the form of FeBi5Ti3O15-Na2Ti3O7-SrTiO3 at variation of 1 % mol. The variation in concentration also results in variable particle sizes, which are between 0.88 µm - 8.23 µm. The dielectric constant (ɛr) obtained is 7.214 and 12.029 at the Curie temperature (Tc) 300 ºC with the material impedance (Z) 136 kΩ and 137 kΩ. |
|---|
| Kata kunci | Bi0,5Na0,5TiO3-SrTiO3 Doping Fe2O3, solid state reaction, konstanta dielektrik |
|---|
| Pembimbing 1 | Dr. -Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Prof. Dr. -Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2019 |
|---|
| Jumlah Halaman | 4 |
|---|
| Tgl. Entri | 2019-07-14 12:29:12.321116 |
|---|