| Judul Artikel | PERBEDAAN TINGKAT KEBOCORAN MIKRO RESIN KOMPOSIT NANOHIBRID MENGGUNAKAN BONDING GENERASI VIII BERBAHAN PELARUT ETANOL DAN ISOPROPANOL DENGAN TEKNIK SELF-ETCH (Kajian In Vitro) |
|---|
| Abstrak (Bhs. Indonesia) | Kebocoran mikro pada tumpatan akan mengakibatkan terjadinya karies sekunder. Pengerutan resin komposit nanohibrid dapat terjadi selama proses polimerisasi dan dipengaruhi dengan pemilihan bahan bonding yang memiliki bahan pelarut yang berbeda seperti bahan pelarut etanol dan isopropanol. Penelitian ini bertujuan untuk mengetahui dan menganalisis perbedaan tingkat kebocoran mikro bahan bonding generasi VIII berbahan pelarut etanol dan isopropanol dengan teknik self-etch menggunakan resin komposit nanohibrid. Jenis penelitian merupakan eksperimental laboratoris dan sampel dibagi ke dalam 4 kelompok. Kelompok I adalah bahan bonding berbahan pelarut etanol dengan teknik total-etch sebagai kontrol, kelompok II adalah bahan bonding berbahan pelarut isopropanol dengan teknik total-etch sebagai kontrol, kelompok III adalah bahan bonding berbahan pelarut etanol dengan teknik self-etch, dan kelompok IV adalah bahan bonding berbahan pelarut isopropanol dengan teknik self-etch. Tingkat kebocoran mikro diuji dengan menggunakan mikroskop stereo. Hasil yang diperoleh dilakukan uji statistik dengan uji Kruskal-Wallis didapatkan hasil perbedaan bermakna pada semua kelompok perlakuan (sig=0,018, p<0,05). Simpulan penelitian ini adalah bahan bonding berbahan pelarut isopropanol dengan teknik self-etch memiliki tingkat kebocoran mikro lebih rendah dibandingkan bahan bonding berbahan pelarut etanol dengan teknik self-etch yang memiliki tingkat kebocoran mikro lebih tinggi. |
|---|
| Abtrak (Bhs. Inggris) | Microleakage of restoration will result in secondary caries. Shrinkage of nanohybrid composite resin dental restoration can be occurred during the polymerization process due to solvent content of bonding materials, for example between ethanol and isopropanol. This study aimed to identify and analyze the microleakages level difference of 8th generation bonding containing ethanol and isopropanol solvents with self-etch technique for nanohybrid resin composite. This research was an experimental research laboratory and samples were divided into four groups. Group I was bonding material containing ethanol solvent with total-etch technique as control group. Group II was bonding containing isopropanol solvent with total-etch technique as control group. Group III was bonding material containing ethanol solvent with self-etch technique. Group IV was bonding material containing isopropanol solvent with self-etch technique. The microleakage level tested with stereo microscope. The results were statistically using Kruskal-Wallis test and showe significant difference between groups (sig=0,018, p<0,05). The conclusion of this study was bonding agent containing solvent isopropanol with self-etch technique has the lower rate of microleakage in comparison to bonding agent containing ethanol solvent. |
|---|
| Kata kunci | Bonding generasi VIII, etanol, isopropanol, self-etch, kebocoran mikro |
|---|
| Pembimbing 1 | drg. Setiadi Warata Logamarta, Sp.Ort |
|---|
| Pembimbing 2 | drg. Irfan Dwiandhono, Sp. KG |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2019 |
|---|
| Jumlah Halaman | 96 |
|---|
| Tgl. Entri | 2019-01-18 09:31:02.290116 |
|---|