| Judul Artikel | DESINFEKSI Echerichia coli DENGAN FOTOKATALIS TIO2-Ag-Ag2O MENGGUNAKAN LAMPU TUNGSTEN |
|---|
| Abstrak (Bhs. Indonesia) | Fotokatalis TiO2-Ag-Ag2O telah berhasil dibuat dengan menggunakan metode photodeposisi dalam penambahan Ag pada TiO2 dan menggunkan metode sonokimia dalam penambahan pektin sebagai pengontrol ukuran mesopori pada TiO2-Ag yang telah dibuat. Jumlah mol TiO2 : Ag divariasikan sebesar 100:0; 99:1; 98:2; 97:3; dan 96:4. Material ini dikarakterisasi menggunakan X-Ray Diffraction (XRD), Diffuse Reflectance Spectrum (DRS), Fourier Transform Infra Red (FTIR), Scanning Electron Microscope (SEM), dan Brunauer, Emmett, and Teller (BET). Hasil XRD menunjukkan adanya puncak Ag sebagai tanda bahwa Ag telah berhasil masuk pada TiO¬2 serta terbentuk Ag2O. Hasil SEM dan BET menunjukkan ukuran material mencapai ukuran mesopori dan homogen dengan sedikit aglomerasi. TiO2-Ag-Ag2O 96:4 memiliki aktivitas fotokatalitik paling tinggi dalam mendesinfeksi Escherichia coli dalam media cair di bawah lampu tungsten yang diukur menggunakan metode TPC. Persentase yang didapat yaitu sebesar 78,11 % dan dengan variasi berat 2 g/L. Peningkatan aktifitas fotkatalitik dari TiO2-Ag-Ag2O tersebut disebabkan karena adanya efek Localized Surface Plasmon Resonance (LSPR) dari Ag dan juga efek hetero junction dari Ag2O. |
|---|
| Abtrak (Bhs. Inggris) | Photocatalysts TiO2-Ag-Ag2O have been successfully synthesized by using photodeposition method in addition of Ag on TiO2 and using sonokimia method in addition of pectin as mesoporous size controller on TiO2-Ag which has been made. The number of moles of TiO2: Ag is varied by 100: 0; 99: 1; 98: 2; 97: 3; and 96: 4. These materials are characterized using X-Ray Diffraction (XRD), Diffuse Reflectance Spectrum (DRS), Fourier Transform Infra Red (FTIR), Scanning Electron Microscope (SEM), and Brunauer, Emmett, and Teller (BET). The XRD results show the peak of Ag as a sign that Ag has successfully entered on TiO2 and formed Ag2O. The SEM and BET results show the size of the material reaches mesoporous and homogeneous size with slight agglomeration. TiO2-Ag-Ag2O 96: 4 has the highest photocatalytic activity in disinfecting Escherichia coli in liquid media under tungsten lamps measured using the TPC method. The increase in photocatalytic activity of TiO2-Ag-Ag2O is due to the effect of Localized Surface Plasmon Resonance (LSPR) from Ag and also the hetero junction effect of Ag2O. |
|---|
| Kata kunci | TiO2-Ag-Ag2O, fotokatalis, Escherichia coli. |
|---|
| Pembimbing 1 | Tien Setyaningtyas, S.Si., M.Si |
|---|
| Pembimbing 2 | Kapti Riyani, S.Si., M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2018 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2018-01-31 09:05:41.107964 |
|---|