| Judul Artikel | PEMBUATAN PENYERAP GELOMBANG MIKRO BERBASIS Nd3+ - BARIUM FERIT DENGAN METODE SOLID STATE TERMODIFIKASI DAN KARAKTERISASINYA
|
|---|
| Abstrak (Bhs. Indonesia) | Nd3+-barium ferit dibuat dengan menggunakan metode modified solid state reaction. Penelitian ini bertujuan untuk mengetahui temperatur sintering optimum dan menentukan karakteristik struktur kristal, sifat magnetik, dan absorpsi gelombang mikro. Dalam penelitian ini digunakan variasi suhu sinter yaitu 600 dan 800 ℃ dengan waktu tahan selama 5 jam. Sampel tanpa sintering (hanya presintering) digunakan sebagai kontrol agar terlihat pengaruh temperatur sintering. Selanjutnya, sampel dikarakterisasi menggunakan XRD, VSM, dan VNA. Hasil XRD menunjukkan telah terbentuk fasa Nd3+-barium ferit pada sampel tanpa sintering. Besarnya ukuran partikel sebanding dengan meningkatnya temperatur sintering. Dengan menggunakan persamaan Debye-Scherrer didapatkan rata-rata ukuran kristal 14,69 nm pada sampel tanpa temperatur sintering dan terus membesar hingga 43,61 nm pada temperatur sinter 800 ℃. Nilai koersivitas dipengaruhi besarnya ukuran partikel. Koersivitas terendah dimiliki sampel BNF dan BNF1 yaitu bernilai 0,0168 dan 0,023 Tesla. Selain itu, temperatur sintering turut menurunkan saturasi magnetik material. Berdasarkan grafik hubungan RL dan frekuensi, sampel BNF1 memiliki RL magnitude terbesar yaitu -26 dB dan lebar bandwidth mencapai 1,56 GHz. |
|---|
| Abtrak (Bhs. Inggris) | Nd3+ -barium ferrite is made by using modified solid state reaction method. This study aims to determine the optimum sintering temperature and determine the characteristics of crystal structure, magnetic properties, and microwave absorption. In this study, used sinter temperature variations of 600 and 800 ℃ with a holding time for 5 hours. Samples without sintering (just presintering) are used as controls to show the effect of sintering temperatures. Furthermore, samples were characterized using XRD, VSM, and VNA. The XRD results showed that Nd3+ -barium ferrite phase was formed on the sample without sintering. The size of the particle is proportional to the increase in sintering temperature. Using the Debye-Scherrer equation we obtained an average crystal size of 14.69 nm in a sample without sintering temperature and continued to expand to 43.61 nm at a sinter temperature of 800 ℃. Coercivity value influenced size of particle size. The lowest coercivity of BNF and BNF1 samples is 0.0168 and 0.023 Tesla. In addition, the sintering temperature also decreases the magnetic saturation of the material. Based on the RL and frequency relationship graphs, the BNF1 sample has the largest RL magnitude of -26 dB and the bandwidth width reaches 1.56 GHz. |
|---|
| Kata kunci | gelombang mikro, Nd3+-barium ferit, temperatur sintering |
|---|
| Pembimbing 1 | Dr. -Ing. Wahyu Widanarto |
|---|
| Pembimbing 2 | Drs. Sunardi, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2017 |
|---|
| Jumlah Halaman | 6 |
|---|
| Tgl. Entri | 2017-10-16 23:31:42.439453 |
|---|