| NIM | H1E013009 |
|---|
| Namamhs | INNAS AMALIYA FATYADI |
|---|
| Judul Artikel | PEMBUATAN ELEKTROLIT KACA ZINC TELLURITE DENGAN DOPING Li+ DAN KARAKTERISASINYA |
|---|
| Abstrak (Bhs. Indonesia) | Elektrolit kaca zinc tellurite telah dibuat menggunakan metode melt quenching pada temperatur 850 ℃ dilanjutkan dengan proses annealing pada temperatur 300 ℃ selama 3 jam, dengan komposisi x Li2O : 15 ZnO : (85-x) TeO2 (dimana x = 0; 5,10 dan 15 dalam % mol). Sifat termal elektrolit kaca zinc tellurite meliputi temperatur transisi kaca (Tg) dikarakterisasi menggunakan Differential Scanning Calorimetry (DSC). Pengaruh penambahan Li2O terhadap struktur dan konduktivitas ionik elektrolit kaca masing-masing dipelajari dengan menggunakan X-ray Diffraction (XRD) dan LCR meter. Pola difraksi XRD yang diperoleh menunjukkan bahwa struktur elektrolit merupakan struktur amorf dengan faktor stabilitas termal di atas 80 ℃ kecuali untuk LiZT2. Pada sampel LiZT2 terdapat dua peak yang muncul, peak ini menunjukkan fase Li2TeO4. Konduktivitas ionik elektrolit kaca menurun dengan bertambahnya konsentrasi Li2O. Nilai konduktivitas ionik tertinggi elektrolit kaca sebesar 2,65〖×10〗^(-7) S/cm yang ditunjukkan oleh elektrolit kaca zinc tellurite yang didoping 0 % mol Li2O pada temperatur 100 ℃ dan 100 Hz. |
|---|
| Abtrak (Bhs. Inggris) | Zinc Tellurite glass electrolyte has been made using melt quenching method at 850 ℃ followed by annealing process at temperature of 300 ℃ for 3 hours.with composition x Li2O: 15 ZnO: (85-x) TeO2 (where x = 0; 5,10 and 15 in% mole). The thermal properties of zinc tellurite glass electrolyte included glass transition temperature (Tg) characterized by Differential Scanning Calorimetry (DSC). The effect of Li2O addition on the structure and ionic conductivity of glass electrolyte were studied using X-ray Diffraction (XRD) and LCR meter. The obtained XRD diffraction pattern shows that the electrolyte structure is an amorphous structure with superior thermal stability factor above 80 ℃ except for LiZT2. In the LiZT2 sample there are two peaks that appear, this peak shows the Li2TeO4 phase. The ionic conductivity of the glass electrolyte decreases with increasing concentration of Li2O. The highest ionic conductivity value of glass electrolyte is 2,65〖×10〗^(-7) S/cm shown by zinc tellurite glass electrolyte doped 0% mol Li2O at temperature of 100 ℃ and 100 Hz. |
|---|
| Kata kunci | Baterai ion Lithium, Elektrolit Kaca Zinc Tellurite, Konduktivitas Ionik |
|---|
| Pembimbing 1 | Dr.-Ing Wahyu Widanarto |
|---|
| Pembimbing 2 | Wahyu Tri Cahyanto, Ph.D |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2017 |
|---|
| Jumlah Halaman | 4 |
|---|
| Tgl. Entri | 2017-08-11 10:25:13.650668 |
|---|