| Judul Artikel | PERBANDINGAN KEKUATAN GESER PERLEKATAN LINER BULK-FILL FLOWABLE COMPOSITE DAN FIBER REINFORCED COMPOSITE PADA DENTIN PASCAAPLIKASI BONDING GENERASI V DAN VII
|
|---|
| Abstrak (Bhs. Indonesia) | Teknik restorasi sandwich adalah teknik restorasi yang menggunakan dua bahan restorasi yang berbeda dalam satu kavitas sebagai liner dan pelapis liner. Salah satu faktor yang mempengaruhi keberhasilan teknik restorasi sandwich adalah kekuatan perlekatan bahan liner yang digunakan pada dentin. Penelitian ini bertujuan untuk mengetahui perbandingan kekuatan geser perlekatan liner bulk-fill flowable composite dan fiber reinforced composite pada dentin pascaaplikasi bonding generasi V dan VII. Penelitian ini menggunakan 32 gigi premolar atas dan dibagi ke dalam 4 kelompok penelitian secara acak. Kelompok A menggunakan liner bulk-fill flowable composite dan bonding generasi V. Kelompok B menggunakan liner bulk-fill flowable composite dan bonding generasi VII. Kelompok C menggunakan liner fiber reinforced composite dan bonding generasi V. Kelompok D menggunakan liner fiber reinforced composite dan bonding generasi VII. Kekuatan geser perlekatan diuji menggunakan Universal Testing Machine dengan kecepatan crosshead 1 mm/menit sampai terjadi kegagalan perlekatan. Data penelitian dianalisis menggunakan uji One Way ANOVA dan uji LSD. Berdasarkan hasil penelitian, penggunaan liner bulk-fill flowable composite pascaaplikasi bonding generasi V menghasilkan kekuatan geser perlekatan liner pada dentin yang paling tinggi. |
|---|
| Abtrak (Bhs. Inggris) | Sandwich restoration is a technique in restoration that use two different restorative materials in a cavity as a liner and final restoration. One of the factors that influencing the succeed of sandwich restoration technique is the bond strength between liner and dentin. The aim of this research was to compare the shear bond strength of liner bulk-fill flowable composite and fiber reinforced composite on dentin post-application of fifth and seventh generation bonding agent. The research was using 32 upper premolars and randomly devided into 4 groups. Group A was using liner bulk-fill flowable composite and fifth generation bonding agent. Group B was using liner bulk-fill flowable composite and seventh generation bonding agent. Group C was using liner fiber reinforced composite and fifth generation bonding agent. Group D was using liner fiber reinforced composite and seventh generation bonding agent. The shear bond strength value was tested using a Universal Testing Machine at a crosshead speed of 1 mm/min until bonding failure occurred. Data was analyzed using One Way ANOVA test and LSD test. Based on the result of this research, the use of liner bulk-fill flowable composite post-application of fifth generation bonding agent yielded the highest shear bond strength of liner on dentin. |
|---|
| Kata kunci | Kekuatan geser perlekatan, bulk-fill flowable composite, fiber reinforced composite, bonding generasi V, bonding generasi VII, shear bond strength, fifth generation bonding agent, seventh generation bonding agent |
|---|
| Pembimbing 1 | drg. Irfan Dwiandhono, Sp.KG. |
|---|
| Pembimbing 2 | drg. Dian Noviyanti Agus Imam, M.DSc. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2017 |
|---|
| Jumlah Halaman | 18 |
|---|
| Tgl. Entri | 2017-08-03 20:12:08.349737 |
|---|