| Judul Artikel | PENGARUH TEMPERATUR SINTERING TERHADAP STRUKTUR DAN SIFAT MAGNET PADA Nd3+-BARIUM FERIT SEBAGAI PENYERAP GELOMBANG MIKRO |
|---|
| Abstrak (Bhs. Indonesia) | Saluran udara tegangan ekstra tinggi (SUTET), peralatan elektronik seperti microwave oven, dan alat komunikasi seperti handphone merupakan sumber-sumber yang dapat menghasilkan radiasi gelombang elektromagnetik. Radiasi gelombang mikro tersebut dapat mengganggu kesehatan manusia, seperti meningkatnya detak jantung, timbul rasa gelisah dan tidak fokus. Berdasarkan permasalahan tersebut, dibutuhkan material yang mampu meredam atau menyerap gelombang mikro agar tidak berbahaya bagi manusia. Sebuah material penyerap gelombang mikro neodimium barium ferit dengan komposisi kimia 0,8BaO: 0,2Nd2O3: 6Fe2O3 dibuat menggunakan metode solid state reaction pada temperatur sintering 1000, 1100, dan 1200 °C. Material ini dikarakterisasi menggunakan XRD, VSM, dan VNA masing-masing guna mengetahui ukuran partikel, fase dan sifat magnetik serta kemampuan dalam menyerap gelombang mikro. Hasil karakterisasi menunjukkan bahwa fase neodimium barium ferit terbaik diperoleh oleh temperatur sintering 1000 °C. Nilai Ms dari material ini meningkat dari 40,86 ke 53,41 hingga 55,64 emu/g, tetapi nilai Hc menurun dari 0,392 ke 0,337 hingga 0,111 T seiring dengan meningkatnya temperatur sintering. Ferit pada temperatur sintering 1000 °C ini mampu menyerap gelombang mikro dengan RL sebesar -24,6; -17,8; dan -11 dB masing-masing pada 8,2; 9,42; dan 10,34 GHz dengan lebar pita 1,38 GHz. Dengan demikian, ferit ini sangat menjanjikan untuk digunakan sebagai material penyerap gelombang mikro dalam X-band. |
|---|
| Abtrak (Bhs. Inggris) | Extra-high voltage air lines (SUTET), electronic equipment such as microwave ovens, and communication devices such as mobile phones are sources that can produce electromagnetic wave radiation. Microwave radiation can interfere human health, such as heartbeat, anxiety and unfocused. Based on these problems, needed materials that can reduce or absorb microwaves to be harmless to humans. A barium neodymium ferrite is microwave absorbent material with a chemical composition 0,8BaO: 0,2Nd2O3: 6Fe2O3 was prepared using solid state reaction method at sintering temperature of 1000, 1100, and 1200 °C. The effect of sintering temperature on particle size, phases and magnetic properties of barium neodymium ferrite and its ability to absorb microwaves are respectively characterized by XRD, VSM, and VNA. The characterization results show that the best phase of barium neodymium ferrite is obtained at a sintering temperature of 1000 °C. The Ms value of this ferrite increases from 40.86 to 55.64 emu/g. While the value of Hc decreased from 0.392 to 0.111 T along with increasing sintering temperature. Ferrite is able to absorb microwaves with RL of -24.6; -17,8; and -11 dB respectively at 8.2; 9.42; and 10.34 GHz with 1.38 GHz bandwidth. Thus, this ferrite is very promising for using as a microwave absorbent material in X-band. |
|---|
| Kata kunci | radiasi gelombang mikro, sintering, barium neodimium ferit, fase, sifat magnetik |
|---|
| Pembimbing 1 | Dr.-Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2017 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | 2017-08-03 09:07:21.322373 |
|---|