| Judul Artikel | PERBEDAAN KARAKTERISTIK MORFOLOGI MIKROSTRUKTUR DAN KEKERASAN NANOKOMPOSIT ALUMINA-SILICA-PARTIALLY STABILIZED ZIRCONIA 17:33:50, 13:27:60, 10:20:70 SEBAGAI MATERIAL PASAK GIGI |
| Abstrak (Bhs. Indonesia) | Pasak gigi merupakan batangan berbentuk kerucut atau silindris yang disemenkan ke dalam saluran akar sebagai retensi bagi inti atau mahkota. Material penyusun pasak gigi dapat berupa logam, fiber reinforced composite, atau keramik. Pasak keramik berbahan dasar zirkonia digunakan karena zirkonia memiliki kekuatan dan ketangguhan retak yang tinggi, tetapi zirkonia memiliki sifat kekerasan yang rendah sehingga membutuhkan tambahan bahan lain seperti alumina dan silika untuk meningkatkan kekerasan material. Penelitian ini bertujuan untuk melihat perbedaan karakteristik morfologi mikrostruktur dan nilai kekerasan nanokomposit keramik alumina-silica-partially stabilized zirconia dengan perbandingan massa 17:33:50, 13:27:50 dan 10:20:70. Metode penelitian yang digunakan adalah eksperimental laboratoris dengan 18 sampel yang dibagi ke dalam 3 kelompok yang kemudian diuji dengan x-ray diffractometer, scanning electron microscope dan microvickers hardness tester. Hasil penelitian menunjukkan adanya aglomerat pada morfologi mikrostruktur serbuk filler setiap kelompok, terlihat adanya struktur geopolimer pada permukaan sampel nanokomposit setiap kelompok, serta nilai kekerasan microvickers yang berbeda antar kelompok. Nilai kekerasan kelompok 1 yaitu 76,65 VHN, pada kelompok 2 yaitu 59,35 VHN, dan pada kelompok 3 yaitu 52,73 VHN. Simpulan penelitian: ada perbedaan karakteristik morfologi mikrostruktur dan nilai kekerasan nanokomposit alumina-silica-partially stabilized zirconia 17:33:50, 13:27:50 dan 10:20:70. Nilai rata-rata kekerasan kelompok 1 adalah yang tertinggi dan telah mencapai nilai kekerasan komposit dalam kedokteran gigi dan nilai kekerasan dentin. |
| Abtrak (Bhs. Inggris) | Dental post is a conical or cylindrical bar that is cemented into the root canals as retention for the core or crown. The material for dental post could be metal, fiber reinforced composite, or ceramic. Zirconia-based ceramic posts were to be used due to the high strength and fracture toughness of zirconia, but it had low hardness properties which required additional materials such as alumina and silica to increase the material’s hardness. This study aims to examine the differences in microstructural morphology characteristic and hardness of alumina-silica-partially stabilized zirconia with mass ratio of 17:33:50, 13:27:50 and 10:20:70. Method of this research was laboratory experimental with 18 samples that were divided into 3 groups, which then were tested by x-ray diffractometer, scanning electron microscope and microvickers hardness tester. The results showed that there were agglomerates on the morphological microstructure of filler powder in each group, geopolimer structures were seen on the surface of nanocomposite samples and there are differences in hardness values between the groups. The value of microvickers hardness obtained from group 1 is 76.65 VHN, from group 2 is 59,35 VHN, and from group 3 is 52,73 VHN. The conclusion of this research is that there are differences in morphological microstructure characteristic and hardness on alumina-silica-partially stabilized zirconia 17:33:50, 13:27:50 and 10:20:70. The hardness mean value of group 1 is the highest and has reached the hardness value of dental composite as well as the hardness value of dentine. |
| Kata kunci | Alumina, silika, zirkonia, pasak gigi, kekerasan |
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar Purwasasmita, M.Eng |
| Pembimbing 2 | drg. Irfan Dwiandhono, Sp.KG |
| Pembimbing 3 | |
| Tahun | 2017 |
| Jumlah Halaman | 20 |
| Tgl. Entri | 2017-07-14 06:17:35.685144 |