| Judul Artikel | PENGARUH PENGGUNAAN NANO HYDROXIAPATITE, MINERAL TRIOXIDE AGGREGATE DAN CALCIUM HYDROXIDE SEBAGAI AGEN PULP CAPPING TERHADAP JUMLAH MAKROFAG DAN DENTIN REPARATIF (Studi Penelitian pada Tikus Sprague Dawley) |
|---|
| Abstrak (Bhs. Indonesia) | Pulp capping merupakan perawatan endodontik untuk mempertahankan vitalitas jaringan pulpa yang mengalami perforasi selapis tipis atap pulpa. Nano hydroxyapatite (nHA) merupakan material bahan terbaru di kedokteran gigi yang bisa digunakan sebagai agen pulp capping selain calcium hydroxide (Ca(OH)2) dan mineral trioxide aggregate (MTA). Penelitian ini bertujuan untuk mengetahui perbedaan pengaruh penggunaan nHA, MTA, dan Ca(OH)2 sebagai agen pulp capping terhadap jumlah makrofag dan dentin reparatif. Penelitian ini menggunakan metode ekperimental laboratoris post test only control group design. Teknik pengambilan sampel yang digunakan yaitu random sampling sehingga didapatkan jumlah sampel sebanyak 32 ekor tikus sprague dawley dibagi menjadi 8 kelompok dan dibagi dalam dua waktu yaitu 3 hari dan 6 minggu. Tikus dianestesi menggunakan ketamin, kemudian gigi molar rahang atas dipreparasi sampai pulpa mengalami perforasi dan diberi aplikasi bahan nHA, MTA, dan Ca(OH)2. Tikus didekapitasi setelah diberi perlakuan dan dilakukan pengambilan gigi molar atas untuk dibuat preparat histologi dengan pewarnaan hematoksilin eosin (HE). Data jumlah makrofag dianalisis menggunakan uji statistik one way ANOVA dilanjutkan dengan uji Post Hoc LSD. Simpulan penelitian ini adalah terdapat perbedaan pengaruh bahan nHA, MTA dan Ca(OH)2 terhadap jumlah makrofag dalam waktu 3 hari dan tidak terdapat pengaruh bahan nHA, MTA dan Ca(OH)2 terhadap dentin reparatif dalam waktu 6 minggu.
|
|---|
| Abtrak (Bhs. Inggris) | Pulp capping is defined as one of the endodontic treatments aimed to maintain the vitality of the perforated pulp tissue. Aside from calcium hydroxide (Ca(OH)2) and mineral trioxide aggregate (MTA), nano hydroxiapatite (nHA) is the most recent dental material used for pulp capping agent. This study was aimed to compare the application of nHA, MTA, and Ca(OH)2 as pulp capping agents on the macrophage counts and reparative dentin. This research was an experimental laboratory study with post test only control group design. Random sampling was used as sampling method, 32 Sprague Dawley Rats were randomly divided into 8 groups each group was then subdivided into 2 groups based on the observation time: 3 and 6 days. The rats were anesthetized with ketamine, preparation was done in molar tooth of the rats until the pulp perforated, followed by the application of nHA, MTA, and Ca(OH)2. The rats were decapitated afterbeing treated, the molar teeth were extracted, processed into histological specimens and stained with Hematoxylin Eosin (HE). The macrophages count were analyzed with one way ANOVA and Post Hoc LSD. The conclusion of this research is the significance in makrofag counts on the 3rd day after nHA, MTA and Ca(OH)2 application, and no significance in dentin reparative on the 6th weeks after nHA, MTA and Ca(OH)2 application. |
|---|
| Kata kunci | Pulp capping, calcium hydroxide, mineral trioxide aggregate, nano hydroxiapatite, makrofag, dentin reparatif |
|---|
| Pembimbing 1 | drg. Setiadi W Logamarta Sp.Ort |
|---|
| Pembimbing 2 | Dr. drg. A Haris Budi Widodo M.Kes., A.P.,S.IP.,S.E. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 17 |
|---|
| Tgl. Entri | 2016-11-20 16:11:40.205505 |
|---|