| Judul Artikel | KARAKTERISASI SIFAT MEKANIK DAN SIFAT OPTIK NANOKOMPOSIT DENGAN EPOKSI RESIN-TiO2 DOPING CARBON NANOTUBE |
|---|
| Abstrak (Bhs. Indonesia) | Lapisan tipis nanokomposit yang terdiri dari epoksi resin-TiO2 dengan variasi penambahan doping carbon nanotube 0,2 % dan 0,6 % telah berhasil dibuat. Sifat mekanik nanokomposit ini diuji untuk mengetahui nilai kuat tarik dan modulus elastis. Sementara uji sifat optik dilakukan untuk melihat morfologi permukaan. Karakterisasi sifat mekanik dengan menggunakan uji tarik menunjukkan bahwa pengaruh penambahan titanium dioksida pada sampel epoksi resin memiliki sifat elastis dan memiliki nilai kekuatan tarik 22,75 MPa, sedangkan nilai modulus elastis pada sampel tersebut diperoleh sebesar 615 MPa. Penambahan doping carbon nanotube 0,2 % dan 0,6 % mengalami penurunan sebesar 18,75 MPa dan 17,54 MPa. Nilai modulus elastisitas pada penambahan doping carbon nanotube 0,6 % memiliki nilai sebesar 415 MPa dan bersifat cukup elastis. sedangkan pada penambahan doping carbon nanotube 0,2% memiliki nilai 0 MPa hal ini menunjukkan bahwa sampel tesebut memiliki sifat yang getas, mudah patah. Hal ini terjadi karena pada saat penambahan massa hardener tidak sesuai dengan sampel yang dibuat sehingga pada saat proses curing, dimana proses pengeringan sampel lapisan tipis tersebut mengalami polimerisasi sehingga terjadi penurunan nilai kekuatan tarik dan nilai modulus elastisitas yang diperoleh. Karakterisasi sifat optik dengan menggunakan uji SEM menunjukan lapisan tipis epoksi resin – TiO2 dan carbon nanotube terlihat butir yang rapat dan seragam serta memiliki ketabalan yang bervariasi dari 18,8 μm hingga 563 μm . |
|---|
| Abtrak (Bhs. Inggris) | Nanocomposite thin layers composed of epoxy resin-TiO2 with addition of doping carbon nanotubes variation of 0.2% and 0.6% has been successfully created. The mechanical properties of nanocomposite was tested to determine the value of tensile strength and elastic modulus. While the optical properties of the test was conducted to see the morphology of the surface. The characterization of the mechanical properties by using a tensile test showed that the effect of adding titanium dioxide to the epoxy resin sample has elastic properties and has a tensile strength value of 22.75 MPa, while the value of the elastic modulus of the sample obtained at 615 MPa. The addition of doping carbon nanotubes 0.2% and 0.6% decreased by 18.75 MPa and 17.54 MPa. Extra elastic modulus at 0.6% doping carbon nanotubes have a value of 415 MPa and is quite elastic. whereas the addition of 0.2% doping carbon nanotube has a value of 0 MPa it indicates that the sample tesebut possess a brittle, easily broken. This happens because when the addition of hardener mass does not correspond to samples made so that during the curing process, where the process of drying the thin layer sample polymerized so that a decline in the value of tensile strength and elastic modulus were obtained. Characterization of optical properties using SEM test shows a thin layer of epoxy resin - TiO2 and carbon nanotube looks dense and uniform grain and has ketabalan varied from 18.8 μm to 563 μm. |
|---|
| Kata kunci | Doping, TiO2, CNT, Uji Tarik, SEM |
|---|
| Pembimbing 1 | Wihantoro,M.Sc |
|---|
| Pembimbing 2 | Dr.-Eng Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 7 |
|---|
| Tgl. Entri | 2016-11-11 08:38:45.970113 |
|---|