| Judul Artikel | PENURUNAN NILAI COD DAN BOD DALAM LIMBAH CAIR INDUSTRI TAHU MENGGUNAKAN LAPIS TIPIS MESOPORI FOTOKATALIS TiO2-Ag PADA LAMPU UV DAN LAMPU TUNGSTEN |
| Abstrak (Bhs. Indonesia) | Telah dilakukan penelitian mengenai penurunan nilai COD dan BOD dalam limbah cair industry tahu menggunakan lapis tipis mesopori fotokatalis TiO2-Ag pada lampu UV dan lampu tungsten. Dalam penelitian ini dilakukan beberapa optimasi, diantaranya perbandingan fotokatalis, pH, dan waktu kontak optimum, dan uji kerekatan foto katalis dengan PEG 1000 serta tanpa PEG 1000. Berdasarkan pengujian didapatkan perbandingan optimum fotokatalis TiO2-Ag dalam menurunan nilai COD dan BOD yaitu pada fotokatalis TiO2-Ag 98:2, persen penurunan pada lampu UV secara berturut-turut sebesar 33,76% dan 24,07% , sedangkan padal ampu tungsten 28,15% dan 20,37%. pH optimum fotokatalis TiO2-Ag 98:2 dalam menurunkan COD dan BOD adalah pada pH 11, dengan persen penurunan pada lampu UV secara berturut-turut adalah sebesar 73,51% dan 66,04%, sedangkan lampu tungsten adalah 62,06% dan 56,36%. Waktu kontak optimum fotokatalis yaitu pada jam kelima, dengan persen penurunan COD dan BOD menggunakan lampu UV sebesar 74,92% dan 59,67%, sedangkan lampu tungsten sebesar 68,37 dan 48,21%. Berdasarkan uji kerekatan, didapatkan lapis tipis fotokatalis dengan penambahan PEG 1000 memiliki kemampuan merekat yang lebih baik disbanding tanpa PEG 1000, dengan aktivitasnya dalam menurunkan nilai COD dan BOD pada lampu UV secara berturut-turut dalah 68,25% dan 55,56%, serta 51,27% dan 40,42%. |
| Abtrak (Bhs. Inggris) | The research on COD and BOD decreased levels of tofu wastewater by thin layer mesoporous TiO2-Ag photocatalyst on UV and tungsten lamps has been conducted. In this research, several optimizations has been done, included ratio of photocatalyst, pH, and the optimum contact time, also adhesiveness test photocatalyst with PEG 1000 and without PEG 1000. Based on result, the optimum ratio of TiO2-Ag to decreased COD and BOD was on the TiO2-Ag 98:2 with percent degradation in the UV lamp respectively was 33.76% and 24.07%, while tungsten lamp was 28.15% and 20.37%. The optimum pH TiO2-Ag 98:2 todecreased COD and BOD was at pH 11, the percent degradation in the UV lamp respectively was 73.51% and 66.04%, while the tungsten lamp was 62.06% and 56.36%. The optimum contact time photocatalyst was in the fifth hour, the percent reduction in COD and BOD using UV lamp was 74,92% and 59.67%, while the tungsten lamp was 68.37 and 48.21%. Based on the test of adhesiveness, TiO2-Ag 98:2 thin layer with PEG 1000 obtained a better adhesiveness than without PEG 1000, with activity on the COD and BOD decreased levels on the UV lamp was 68.25% and 55.56%, respectively, and without PEG 1000 was 51.27% and 40.42%. |
| Kata kunci | Fotokatalis, COD, BOD, TiO2-Ag Mesopori. |
| Pembimbing 1 | Kapti Riyani, M.Si. |
| Pembimbing 2 | Tien Setyaningtyas, M.Si. |
| Pembimbing 3 | |
| Tahun | 2016 |
| Jumlah Halaman | 82 |
| Tgl. Entri | 2016-11-09 20:03:48.708419 |