| NIM | H1E012029 |
|---|
| Namamhs | RISKA FEBRIANA |
|---|
| Judul Artikel | PENGARUH VARIASI SUHU SINTERING TERHADAP BAHAN MAGNETIK STRONSIUM NEODIMIUM FERIT SEBAGAI PENYERAP GELOMBANG MIKRO |
|---|
| Abstrak (Bhs. Indonesia) | Penelitian mengenai ferit alam yang di doping dengan neodimium telah dilakukan untuk mengetahui pengaruh suhu sintering terhadap struktur, sifat magnetik dan absorpsi gelombang mikro. Pembuatan sampel dilakukan menggunakan metode solid state reaction dengan komposisi 6Fe2O3:0.8SrO:0.2Nd2O3. Sampel di sintering pada suhu 900 ° C, 1000 ° C and 1100 ° C. Karakterisasi struktur, sifat magnetik dan absorpsi gelombang mikro dilakukan menggunakan XRD, VSM, dan VNA. Hasil karakterisasi menunjukkan bahwa pada suhu 900 ° C terdapat fasa kristal SrNdFeO4 yang terbentuk paling banyak. Sifat magnetik yang meliputi magnetisasi remanen (Mr) dan magnetisasi saturasi (Ms) mengalami peningkatan, sedangkan medan koersivitas (Hc) mengalami penurunan dengan meningkatnya temperatur sintering. Ferit yang diperoleh mempunyai sifat superparamagnetik dengan suseptibilitas magnetik (χm) positif bernilai kecil χm<<1. Sampel menyerap gelombang mikro dalam rentang frekuensi 8 hingga 12 GHz. Sampel dengan suhu sintering pada suhu 1000 °C menujukkan hasil penyerapan yang baik dengan ditandai oleh absorpsi gelombang mikro tertinggi pada frekuensi 8,02 GHz dengan reflection loss (RL) sebesar -31 dB. |
|---|
| Abtrak (Bhs. Inggris) | Research on nature in ferrite doped with neodymium have been conducted to determine the effect of sintering temperature on the structure, magnetic properties and the absorption of microwaves. Sample preparation is done using solid state reaction method with composition 6Fe2O3:0.8SrO:0.2Nd2O3. Samples in sintering at a temperature of 900 ° C, 1000 ° C and 1100 ° C. Characterization of the structure, magnetic properties and the absorption of microwaves was performed using XRD, VSM, and VNA. The results showed that at temperatures of 900 ° C contained crystallyn phase formed SrNdFeO4 most. Magnetic properties which include remanent magnetization (Mr) to saturation magnetization (Ms) increased, whereas the coercivity field (Hc) decreased with increasing temperature sintering. Ferrite obtained has paramagnetic properties with magnetic susceptibility (χm) positive small value χm<< 1. Samples absorb microwaves in the range frequency of 8 to 12 GHz. Samples with temperature sintering at 1000 ° C showed good results with the absorption characterized by the highest absorption of microwaves at a frequency of 8,02 GHz with reflection loss (RL) of -31 dB. |
|---|
| Kata kunci | absorpsi gelombang mikro, metode solid state reaction, stronsium neodimium ferit, suhu sintering, struktur kristal, sifat magnetik.. |
|---|
| Pembimbing 1 | Dr. –Eng Mukhtar Effendi |
|---|
| Pembimbing 2 | Dr. –Ing Wahyu Widanarto |
|---|