| Judul Artikel | PENGARUH Nd3+ TERHADAP STRUKTUR, SIFAT MAGNETIK, DAN SERAPAN GELOMBANG MIKRO PADA MATERIAL STRONSIUM FERIT |
| Abstrak (Bhs. Indonesia) | Pembuatan material magnetik stronsium ferit doping Nd3+menggunakan metode solid state reaction telah berhasil dilakukan. Penelitian ini bertujuan untuk menentukan pengaruh Nd3+ terhadap struktur, sifat magnetik, dan serapan gelombang mikro. Pembuatan (1-x)SrO: xNd2O3 : 6Fe2O3 dimana x = 0; 0,1; 0,2 dan 0,3 mol menggunakan bahan dasar berupa serbuk SrCO3 dengan kemurnian 99%, serbuk Nd2O3 (dengan kemurnian 99%), dan Fe3O4 dari pasir besi alam. Karakterisasi yang dilakukan meliputi pengujian X-Ray Difraction (XRD) untuk mengetahui struktur kristal, Vibrating Sampel Magnetometer (VSM) untuk sifat magnetik suatu material, dan Vector Network Analyzer (VNA) untuk serapan gelombang mikro. Hasil XRD menunjukan semakin banyak penambahan doping Nd3+ maka jumlah fasa SrNdFeO4 semakin bertambah. Fasa tersebut memiliki struktur kristal Tetragonal yang memiliki parameter sel a = b = 3,846 Å, dan c = 12,594 Å. Karakterisik sifat magnetik menunjukan semakin besar penambahan Nd3+ nilai magnetisasi saturasi dan remanansi mengalami penurunan dan nilai medan koersivitas meningkat dan semua sampel masih tergolong material paramagnetik. Sementara itu, penyerapan gelombang terbaik terjadi pada sampel SNF4 dengan penambahan Nd3+ sebanyak 0,3 mol yang menghasilkan nilai reflection loss sebesar -18,9 dB dengan bandwidth frekuensi sebesar 3,9 GHz. Kata kunci : stronsium ferit, solid state reaction, struktur kristal, sifat magnetik, penyerap gelombang mikro |
| Abtrak (Bhs. Inggris) | The synthesis of magnetic materials strontium ferrite doping Nd3+ using solid state reaction method has been successfully. This study aims to determine the effect of Nd3+ on the structure, magnetic properties, and the absorption of microwaves. Making (1-x) SrO: xNd2O3: 6Fe2O3 where x = 0; 0,1; 0,2 and 0,3 mol using basic materials SrCO3 powder form with a purity of 99%, Nd2O3 powder (about 99%), and Fe3O4 of iron sand nature. Characterization was conducted on the testing of X-Ray Difraction (XRD) to determine the crystal structure, Vibrating Sample Magnetometer (VSM) for the magnetic properties of a material, and a Vector Network Analyzer (VNA) for the absorption of microwaves. The XRD results showed the more the addition of doping Nd3+ then SrNdFeO4 growing number of phases. These phases have a crystalline structure Tetragonals who have cell parameters a = b = 3,846 Å and c = 12,594 Å. Characteristics of the magnetic properties showed the greater increase Nd3+ saturation magnetization values and remanansi decreasing and increasing the value of coercivity field and all samples are still classified as paramagnetic material. Meanwhile, the best wave absorption occurs in the sample Nd3+ is SNF4 with the addition of 0,3 moles that produce value reflection loss amounted to -18,9 dB with a frequency bandwidth of 3,9 GHz. Keywords: strontium ferrite, solid state reaction, crystal structure, magnetic properties, microwave absorber |
| Kata kunci | stronsium ferit, solid state reaction, struktur kristal, sifat magnetik, penyerap gelombang mikro |
| Pembimbing 1 | Dr.-Eng Mukhtar Effendi |
| Pembimbing 2 | Wahyu Tri Cahyanto, Ph.D |
| Pembimbing 3 | |
| Tahun | 2016 |
| Jumlah Halaman | 12 |
| Tgl. Entri | 2016-10-17 17:40:06.00894 |