| Judul Artikel | PEMBUATAN MAGNET BARIUM MANGANESE FERRITE MENGGUNAKAN METODE HIBRID SOL-GEL SEBAGAI BAHAN PENYERAP GELOMBANG MIKRO |
|---|
| Abstrak (Bhs. Indonesia) | Penyebaran gelombang mikro semakin meluas, mengakibatkan interferensi elektromagnetik, pencemaran lingkungan dan bahaya terhadap kesehatan, sehingga perlu adanya bahan penyerap gelombang mikro. Bahan penyerap gelombang mikro dapat dimanfaatkan sebagai material pelapis pesawat anti RADAR. Penelitian ini bertujuan untuk mengetahui pengaruh doping Mn4+ pada pembuatan Barium Manganese Ferrite terhadap struktur kristal, sifat magnetik dan penyerapan gelombang mikro. Metode yang digunakan adalah metode hibrid sol-gel. Metode hibrid sol-gel merupakan gabungan metode sol-gel dan solid state reaction. Bahan utama yang digunakan yaitu Ba(NO3)2, MnO2 dan Fe3O4 yang diperoleh dari hasil pemurnian pasir pantai. Bahan dicampurkan menggunakan larutan, sehingga mendapatkan gel pekat, dan dikalsinasi pada 350oC. Kemudian serbuk Barium Manganese Ferrite dikompaksi dan dilakukan sintering pada 1100oC selama 5 jam. Karakterisasi sampel dilakukan menggunakan uji XRD, VSM dan VNA. Hasil karakterisasi XRD membentuk BaFe2,37Mn9,63O19 dominan pada sampel MBF3 konsentrasi doping Mn4+ 0,2 mol, dengan ukuran kristal sebesar 23,74 nm. Hasil uji karakterisasi VSM menunjukkan sifat superparamagnetik dan Ms semakin turun karena pengaruh metode hibrid sol-gel dalam memperkecil ukuran. Begitupun hasil karakterisasi VNA menunjukkan MBF3 memiliki nilai serapan optimum, yakni pada lebar frekuensi 8 – 12 GHz nilai gelombang yang diserap sebesar -13.0523 dB. Sehingga nilai serapan erat kaitannya dengan Ms, semakin kecil nilai Ms, semakin dalam serapan pada material. |
|---|
| Abtrak (Bhs. Inggris) | Microwave wide-spread results electomagnetic interference, environmental pollution and hazards for health, thus microwave (MW) absorber is needed. The microwave absorbent material can be used as a coating material on air anti RADAR. This research aims to determine effect of Mn4+ on crystal structure, magnetic properties, and microwave absorbation of Barium Manganese Ferrite. The ferrites were prepared using hybrid sol-gel method, which is a combination between sol-gel method and solid state reaction. Commercial Ba(NO3)2 and MnO2 were used as raw materials, meanwhile Fe3O4 were obtained from purification of natural iron sand. Mixed material using a solution, so that gel were obtained, it was calcinated. Then, Barium Manganese Ferrite powder was compacted and sintered at 1100 oC for 5 hours. Structure, magnetic properties and microwave absorbtion of the ferrites were characterized using XRD, VSM, and VNA. Characterization results of XRD show that Barium Manganese Ferrite BaFe2,37Mn9,63O19 dominated in MBF3 sample or 0,2 mol of Mn4+ doping concentration, with size of crystall 23,74 nm. All samples reveals superparamagnetic character and decrease of Ms value, that is proved by VSM. This is caused by effect of hybrid sol-gel method to minimize size. Likewise, VNA characterization shows MBF3 has the best absorbtion. Value of reflection loss (RL) at is -13,0523 dB and absorption of width frequency 8-12 GHz. Thus, absorption value has firm relevancy with Ms, the smaller Ms value, the deeper absorption of material become. |
|---|
| Kata kunci | Gelombang mikro, Hibrid Sol-gel, Barium Manganese Ferrite. |
|---|
| Pembimbing 1 | Dr. Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr. Eng. Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | 2016-10-17 04:53:21.725789 |
|---|