| Judul Artikel | Karakterisasi Sifat Mekanik, Optik, Dan Listrik Kitosan PEG 4000 Doping Garam LiClO4 Sebagai Membran Polimer Elektrolit Baterai |
|---|
| Abstrak (Bhs. Indonesia) | Pada penelitian ini telah dilakukan karakterisasi sifat mekanik, optik, dan listrik dari membran polimer elektrolit Kitosan PEG 4000 doping garam LiClO4. Proses fabrikasi meliputi fabrikasi kitosan- PEG 4000 dengan konsentrasi 80% dan 20%, dan fabrikasi kitosan PEG 4000 didopingkan dengan garam LiClO4 sebanyak 15% dan 75%. Hasil pengujian sifat mekanik pada kitosan- PEG 4000 didapat nilai kuat tarik 448,15 MPa pendopingan garam LiClO4 sebanyak 15% dan 75% menghasilkan nilai kuat tarik masing masing 448,15 MPa dan 10,52 MPa, pada pengujian sifat listrik nilai konduktivitas yang diperoleh pada kitosan– PEG 4000 adalah 1,26.10^(-11)S/cm, dengan pendopingan garam LiClO4 sebanyak 15% dan 75% menghasilkan nilai konduktivitas masing masing 1,44.10^(-11)S/cm dan 1,45.10^(-8)S/cm. Pada sifat optik hasil yang diperoleh pada Kitosan- PEG 4000 adalah pelemahan sinyal ganda pada bilangan gelombang 3523 cm^(-1) dan 3560 cm^(-1), pelemahan sinyal tunggal pada bilangan gelombang 1623 cm^(-1), dan pelemahan sinyal pada bilangan Gelombang 3000 sampai 3700 cm^(-1), penambahan garam LiClO4 15% menunjukkan adanya pelemahan sinyal pada bilangan gelombang 1644 cm^(-1), dan pelemahan sinyal pada bilangan gelombang 3000 sampai 3675 cm^(-1), penambahan garam LiClO4 sebanyak 75% menghasilkan pelemahan sinyal pada bilangan gelombang 2882 cm^(-1). Sedangkan hasil pada pengujian XRD menunjukkan penambahan konsentrasi garam LiClO4 menghasilkan struktur kristal yang semakin amorf.
|
|---|
| Abtrak (Bhs. Inggris) | This research has been done on the characterization of mechanical, optical, and electrical properties of polymer electrolyte membrane of Chitosan PEG 4000 doped with LiClO4 salt. The fabrication process are Chitosan PEG 4000 at the concentration of 80% and 20% and fabrication of Chitosan PEG 4000 doped with LiClO4 salt with concentration of 15% and 75%. The mechanical properties result of Chitosan- PEG 4000 is tensile strength values of 448,15 MPa. The added of LiClO4 salt with concentration of 15% and 75% giving tensile strength result of 448,15 MPa and 10,52 MPa. The electrical properties result on Chitosan- PEG 4000 has given the conductivity value of 1,26.〖10〗^(-11)S/cm. With the added of LiClO4 salt of 15% and 75% has given conductivity values of 1,44.〖10〗^(-11)S/cm and 1,45.〖10〗^(-8)S/cm. The optical properties result of Chitosan PEG 4000 is double signal attenuation at ṽ 3523 cm^(-1) and 3560 cm^(-1), single signal attenuation at ṽ 1623 cm^(-1), broad signal attenuation at ṽ 3000 to 3700 cm^(-1). The added of 15% LiClO4 salt show signal attenuation at ṽ 1644 cm^(-1). And the broad signal attenuation at ṽ 3000 to 3675 cm^(-1). The added of 75% LiClO4 salt has given signal attenuation at ṽ 2882 cm^(-1). And the result of XRD test shows the added of LiClO4 salt concentration resulted in an increasingly amorphous crystaline structure.
|
|---|
| Kata kunci | Membran polimer, Elektrolit, Kitosan, PEG 4000, Litium Perklorat |
|---|
| Pembimbing 1 | Wihantoro, S. Si, M. Sc |
|---|
| Pembimbing 2 | Drs. Sunardi, M. Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 89 |
|---|
| Tgl. Entri | 2016-09-15 16:34:51.422899 |
|---|