Artikel Ilmiah : G1G010007 a.n. BAYU VAVA VIOLETA
| NIM | G1G010007 |
|---|---|
| Namamhs | BAYU VAVA VIOLETA |
| Judul Artikel | PENGARUH ANODIZATION CYCLIC PRE-CALCIFICATION HEAT TREATMENT TERHADAP JUMLAH OSTEOBLAS PADA DENTAL IMPLAN BERBAHAN TITANIUM ALLOY (Studi invivo pada tikus wistar galur Sprague dawley) |
| Abstrak (Bhs. Indonesia) | Anodization Cyclic Pre-Calcification Heat Treatment (APH) merupakan suatu treatment yang dilakukan untuk membuat implan menjadi lebih biokompatibel. Tujuan penelitian ini untuk mengetahui pengaruh Anodization Cyclic Pre-Calcification Heat (APH) terhadap jumlah osteoblas dental implan berbahan titanium alloy. Penelitian yang dilakukan adalah penelitian eksperimental laboratoris dengan metode penelitian Rancangan Acak Kelompok (RAK) yang terdiri atas dua kelompok APH dan non-APH. Pengambilan sampel dilakukan secara simple random sampling dengan kriteria inklusi tikus jantan, umur 3 bulan dan sehat secara fisik. Kriteria ekslusi yaitu, tikus dengan cacat pada bagian kaki dan mengalami sakit. Berdasarkan hasil perhitungan dengan rumus federer didapatkan besar sampel sebanyak 16 sampel perkelompok. Cara kerja pada penelitian ini dimulai dengan melakukan tindakan profilaksis antibiotik dan anastesi menggunakan ketamin pada seluruh hewan coba. Sampel implan dalam bentuk disc dengan ketebalan 1 mm pada sampel hewan coba kelompok APH dilakukan treatment anodisasi, prekalfikasi dan heat treatment sedangkan kelompok non-APH tidak dilakukan. Proses implantasi dilakukan dengan cara mempreparasi tibia tikus dengan diamond bur. Setelah 3 minggu, tikus didekapitasi untuk dilakukan pengambilan jaringan tibia dan dibuatkan preparat histologi dengan pewarnaan Hematoksilin Eosin (HE) untuk selanjutnya dilakukan penghitungan jumlah osteoblas. Data jumlah osteoblas dianalisis menggunakan Independent T-test sedangkan keberadaan pori hasil anodisasi dilakukan dengan menggunakan uji SEM pada permukaan material implan. Hasil uji SEM pada permukaan material implan terdapat keberadaan pori hasil anodisasi pada kelompok APH. Hasil penghitungan rerata jumlah osteoblas pada kelompok APH didapatkan sebesar 48,50 dan kelompok non-APH sebesar 31,99. Analisis independent t-test menunjukkan bahwa sig <0,05 yang artinya terdapat perbedaan yang bermakna pada jumlah osteoblas pada kelompok APH dan non-APH. |
| Abtrak (Bhs. Inggris) | Anodization Cyclic Pre-Calcification Heat Treatment (APH) Is a treatment that goes into making implant become more biocompatible. The purpose of this research to know influence anodization cyclic pre-calcification heat (APH ) on the number of osteoblast dental based on implant titanium alloy. Research conducted is research experimental laboratoris with the draft random research group Which is made up of two groups aph and non-aph .The sample collection done in random sampling simple criteria of inclusion of male rats , the age of 3 months and healthy Physically . Exclusion criteria is a rat with defects in his legs and suffered pain .Calculation based on the results obtained large sample as many as 16sample a group. How to work in research was started take action prophylactic antibiotics and anesthetized using ketamine in all rats. Sample implant in the form of a disc with 1 mm thickness in samples of animal groups aph treatment do the anodization, precalcification and heat treatment while group non-aph not done. The process of implantation done by means of preparation tibia with diamond bur . After 3 weeks , rats decapitalized to To take bone tissue on tibia and propose histologycal examination with staining haematoxylin eosin (HE) and do the calculation of the number of osteoblast. The number of osteoblast analyzed using Independent T-test while the existence of the results pore of anodization conducted using the SEM on the surface of the material implant. The results of the SEM on the surface of the material implant there are the existence of pore anodization results in the APH group. The calculation on the number of osteoblast APH group obtained by 48,50 and the non-APH group by 31,99. Independent T-test analysis shows that the results ( sig. <0,05 ) which means there are significant differences in the number of osteoblast APH and non-APH. |
| Kata kunci | Anodisasi, prekalsifikasi, osteoblas, dental Implan, Ti-6Al-7Nb |
| Pembimbing 1 | A. Haris Budi Widodo |
| Pembimbing 2 | Priyo Susatyo |
| Pembimbing 3 | |
| Tahun | 2016 |
| Jumlah Halaman | 28 |
| Tgl. Entri | 2016-08-10 05:55:40.973664 |