| Judul Artikel | PEMANFAATAN LIMBAH STYROFOAM SEBAGAI MEMBRAN POLIMER ELEKTROLIT DARI KOMPOSIT POLISTIRENA TERSULFONASI, KITOSAN-VANILIN, ZEOLIT TERKALSINASI DENGAN PENAMBAHAN POLIETILEN GLIKOL 400 |
|---|
| Abstrak (Bhs. Indonesia) | Pembuatan membran komposit polistirena tersulfonasi (PST), kitosan-vanilin (KV), zeolit alam terkalsinasi (ZAH), dan polietilen glikol 400 (PEG 400) sebagai pemlastis telah dilakukan. PST yang digunakan dalam penelitian ini disintesis dari polistirena limbah styrofoam dengan agen sulfonasi asetil sulfat. Pembuatan membran komposit ini menggunakan metode inversi fasa dengan pencetakan larutan. Seluruh material penyusun membran komposit dilarutkan dalam pelarut dimetil asetamida (DMAc) dengan perbandingan komposisi % (b/b) dan berat total 10 gram. Dalam penelitian ini, dilakukan variasi komposisi PEG 400 dan ZAH untuk mengetahui pengaruhnya terhadap nilai kapasitas tukar kation (KTK) dan nilai swelling degree (SD). Selanjutnya membran komposit dan material penyusunnya dikarakterisasi dengan spektroskopi inframerah. Penelitian ini menunjukkan hasil bahwa penambahan PEG 400 dan ZAH dapat meningkatkan kapasitas tukar kation dan menurunkan swelling degree membran yang dihasilkan. Membran dengan penambahan PEG sebesar 8% memiliki nilai KTK yang paling tinggi yaitu sebesar 25,27 meq/g, sedangkan membran dengan penambahan ZAH sebesar 2% memiliki nilai KTK yang lebih besar daripada ZAH 1%. Namun, penambahan ZAH lebih dari 2% dapat menurunkan nilai KTK. Membran dengan penambahan PEG sebesar 8% memiliki nilai SD yang paling kecil yaitu sebesar 3,58%, sedangkan membran dengan penambahan ZAH sebesar 4% memiliki nilai SD yang lebih kecil yaitu sebesar 0,25 %. Munculnya serapan khas dari masing-masing material penyusunnya pada analisis gugus fungsi menunjukkan membran polimer elektrolit berhasil disintesis dari komposit PST/KV/ZAH dan PEG 400. |
|---|
| Abtrak (Bhs. Inggris) | Composite membranes from sulfonated polystyrene (PST), chitosan-vanillin (KV), calcined natural zeolite (ZAH), and polyethylene glycol 400 (PEG 400) as a plasticizer had been done.PST were synthesized from waste polystyrene styrofoam with acetyl sulfate sulfonation agent.Manufacture of composite membranes used phase inversion method with printing solution.All materials were dissolved in the solvent dimethyl acetamide (DMAc) with a composition ratio % (w/w) and a total weight of 10 grams.The research used compositional variations of ZAH and PEG 400 to determine its effect on the value of the cation exchange capacity (CEC) and the swelling degree (SD).Furthermore, composite membrane and its constituent materials were characterized by infrared spectroscopy.This research showed that addition of PEG 400 and ZAH could improve cation exchange capacity and lowering the degree of swelling resulting membrane.Membrane of PEG 8% has the highest CEC value that is equal to 25.27 meq /g. Membrane with addition of 2% ZAH had a higher CEC than ZAH 1%.The addition of more than 2% ZAH could decreased the value of the CEC.Membrane PEG of 8% had smallest SD value that is equal to 3.58%. Membrane with the addition of 4% ZAH had the lower SD of 0.25%. The analysis of FTIR showed the specific peak from each materials. It showed that electrolyte polymer membrane had been synthesized successfully. |
|---|
| Kata kunci | kitosan-vanilin, membran polimer elektrolit, polistirena, sulfonasi, zeolit terkalsinasi. |
|---|
| Pembimbing 1 | Senny Widyaningsih, S.Si., M.Si |
|---|
| Pembimbing 2 | Dwi Kartika, S.Si., M.Sc |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 2 |
|---|
| Tgl. Entri | 2016-08-09 03:08:24.242948 |
|---|