| Judul Artikel | PEMBUATAN LANTANUM STRONSIUM FERIT DENGAN METODE SOLID STATE REACTION SEBAGAI PENYERAP GELOMBANG MIKRO |
|---|
| Abstrak (Bhs. Indonesia) | Pembuatan material stronsium ferit dengan penambahan La^(3+) dilakukan menggunakan metode solid state reaction dengan komposisi (1-x)SrO:(x)La2O3:6Fe2O¬3, dimana ( mol). Penelitian ini bertujuan untuk menentukan pengaruh penambahan La^(3+) terhadap fasa, sifat magnetik, dan karakteristik absorpsi gelombang mikro. Metode solid state reaction terdiri dari proses pencampuran dengan cara milling selama 20 menit, pemadatan dengan tekanan 1 ton dalam kondisi pengaruh medan magnet 6000 Gauss, dan sintering pada suhu 1100°C selama 3 jam. Karakterisasi yang dilakukan meliputi X-Ray Difraction (XRD), Vibrating Sampel Magnetometer (VSM), dan Vector Network Analyzer (VNA). Hasil penelitian pada keempat sampel menunjukkan bahwa penambahan La^(3+) berpengaruh terhadap ukuran kristal yang semakin homogen dan fasa berubah dengan meningkatnya LaSrFeO. Selain itu, seiring penambahan La^(3+) nilai medan koersivitas (H_c) awalnya menurun kemudian meningkat, nilai magnetisasi saturasi (M_s) dan nilai magnetisasi remanen (M_r) mengalami penurunan, namun nilai magnetisasi saturasi (M_s) dan nilai magnetisasi remanen (M_r) pada mol lebih besar dibandingkan mol. Penyerapan gelombang mikro tertinggi terjadi pada penambahan doping La^(3+) sebanyak 0,15 mol, yaitu -29,91 dB pada frekuensi 10,63 GHz dan memiliki lebar pita penyerapan sebesar 2,73 GHz. Secara keseluruhan, hasil penelitian ini menunjukkan adanya peningkatan performa serapan gelombang mikro yang diakibatkan oleh penambahan lantanum pada stronsium ferit. |
|---|
| Abtrak (Bhs. Inggris) | Manufacturing of stronsium ferit material with La^(3+) as doping has done by using solid state reaction with composition (1-x)SrO:(x)La2O3:6Fe2O¬3, where ( mol). This research aim is to determine the impact of doping La3+ to phase, magnetic properties, and microwave absorption characteristic. Solid state reaction methode concists milling compounding for 20 minutes, solidity with 1 ton pressure under influence of 6000 Gauss magnetic field at 1100°C for 3 hours. Characterization that has done include X-Ray Difraction (XRD), Vibrating Sampel Magnetometer (VSM), dan Vector Network Analyzer (VNA). The result from four sample shows that La^(3+) doping has effect to crystal size which become more homogen and the change of phase as raisment of LaSrFeO. Beside that,coersivity value (H_c) that originally decrease is increasing along with La^(3+) addition, saturation magnetization value (M_s) and remanent magnetization value (M_r) are expressing decrease although saturation magnetization value (M_s) and remanent magnetization value (M_r) at mol is bigger in different from mol. The higest microwave arbsorption value is -29,91 dB with frequency 10,63 GHz and arbsorption band width 2,73 GHz when La^(3+) doping is 0,15 mol. As a whole, this research outcome shows that there is increasement of microwave absorption which caused by lantanum addition to stronsium ferit. |
|---|
| Kata kunci | Kata Kunci : Stronsium ferit, sifat magnetik, penyerap gelombang mikro. |
|---|
| Pembimbing 1 | Dr. -Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Dr. -Ing. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2016-08-05 17:18:38.770479 |
|---|