| Judul Artikel | SINTESIS DAN KARAKTERISASI MEMBRAN ELEKTROLIT DARI KOMPOSIT POLISTIRENA TERSULFONASI/KITOSAN-VANILIN/ ZEOLIT TERKALSINASI DENGAN PENAMBAHAN POLIETILEN GLIKOL SEBAGAI PLASTICIZER |
|---|
| Abstrak (Bhs. Indonesia) | Limbah styrofoam digunakan untuk pembuatan membran elektrolit dari komposit polistirena tersulfonasi, kitosan-vanilin, zeolit terkalsinasi dengan variasi penambahan polietilen glikol. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan polietilen glikol terhadap karakteristik membran komposit serta mengetahui karakteristik membran hasil analisis FTIR, kapasitas tukar kation dan derajat pengembangan. Pembuatan membran komposit menggunakan metode inversi fasa. Hasil analisis FTIR menunjukkan adanya serapan dari gugus fungsi material-material penyusunnya. Nilai kapasitas tukar kation membran komposit lebih tinggi dibandingkan dengan material penyusun membran. Penambahan polietilen glikol mengakibatkan penurunan nilai KTK pada membran komposit. Derajat pengembangan membran komposit dengan penambahan polietilen glikol mengalami kenaikan hingga penambahan polietilen glikol 6%, sedangkan penambahan polietilen glikol 8% mengakibatkan penurunan derajat pengembangan membran. |
|---|
| Abtrak (Bhs. Inggris) | Waste styrofoam is used for manufacturing a composite electrolyte membrane of sulfonated polystyrene, chitosan-vanillin, zeolite calcinated with addition of polyethylene glycol. This research aim to determine of influence addition polyethylene glycol to the characteristic of composite membane . and to know the membrane characteristic based on with FTIR, cation exchange capasity and swelling degree. Manufacture of composite membrane used inverse phase method. FTIR analysis showed that there was absorption of functional group of the materials constituents. The cation exchange capasity (CEC) of the membrane was higher than materials constituent. The addition of polyethylene glycol decrease CEC value on composite membrane. Swelling degree of composite membrane with the addition of polyethylene glycol increased until addition 6%, whereas the addition 8% decreased of swelling degree membrane. |
|---|
| Kata kunci | kitosan-vanilin, membran elektrolit, polietilen glikol, polistirena tersulfonasi |
|---|
| Pembimbing 1 | Senny Widyaningsih, M. Si. |
|---|
| Pembimbing 2 | Dra.Eva Vaulina YD, M. Si. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 2 |
|---|
| Tgl. Entri | 2016-07-26 13:53:05.470924 |
|---|