| Judul Artikel | OPTIMASI SIFAT NANOKOMPOSIT METAKAOLIN-KARBONAT APATIT DENGAN DOPING STRONSIUM DAN COUPLING AGENT KITOSAN UNTUK APLIKASI PLAT IMPLAN |
| Abstrak (Bhs. Indonesia) | Pengembangan material implan kini difokuskan pada biokeramik dengan sifat mekanik dan biokompabilitas serta kemampuan biointegrasi yang baik seperti penggunaan karbonat apatit dan stronsium sebagai doping. Metakaolin dan kitosan sebagai coupling agent diketahui mampu meningkatkan sifat mekanik suatu material. Penelitian ini bertujuan untuk mengetahui karakteristik sifat dan optimasi nanokomposit metakaolin dan karbonat apatit dengan doping stronsium dan coupling agent kitosan yang sesuai untuk aplikasi plat implan. Jenis penelitian merupakan penelitian eksperimental laboratoris dengan metode simple random sampling yang terbagi menjadi empat kelompok sampel, yaitu nanokomposit metakaolin dan karbonat apatit dengan doping stronsium dan coupling agent kitosan dengan perbandingan massa 1:1, 2:1, dan 3:1 serta dengan teknik dip coating. Hasil penelitian menunjukkan pada sifat kimia adanya kelengkapan gugus fungsi namun tidak ditemukan gugus Sr-O, sifat mekanik yang tidak mendekati nilai parameter sifat mekanik tulang kortikal sementara kelompok sampel dengan sifat mekanik terbaik yaitu nanokomposit dengan perbandingan massa 2:1 dan 3:1 menunjukkan adanya sifat bioaktifitas. Simpulan penelitian ini adalah tidak adanya kelompok sampel yang memiliki sifat karakteristik sebagai plat implan namun kelompok sampel dengan sifat mekanik, kimia, dan biologis yang paling optimal adalah nanokomposit metakaolin dan karbonat apatit dengan doping stronsium dan coupling agent kitosan pada perbandingan massa 2:1 dapat berpotensi sebagai inisiator pembentukan tulang dan plat implan pada tulang trabekular. |
| Abtrak (Bhs. Inggris) | Various problem implant plate based on metal and polymer materials when used as fixation for bone defect case induced development of bioceramic for implant plate materials. The development focused on bioceramic materials with good mechanical characteristic and good biocompability along with biointegrity, such as carbonate apatite and stronsium as doping. Metakaolin and addition of chitosan as a coupling agent is known to improve the mechanical properties of material. This study aims to determine the characteristics and optimation of nanocomposite metakaolin-carbonate apatite doped strontium and chitosan as coupling agent for implant plate application, covers the microstructure morphological characteristic, the flexibility, the hardness, functional band and bioactivity. This study is an experimental laboratory research with simple random sampling methode, by dividing the sample into four groups: nanocomposite metakaolin-strontium doped carbonate apatite and chitosan as coupling agent for implant plate with a mass ratio 1:1, 2:1, 3:1, and dip coating technique. The result of chemical characteristic showed a complete functional bond except the Sr-O bond but detected on XRD results as carbonate apatite (Sr-bearing), mechanical characteristic showed neither hardness and flexibility value of nanocomposite approach mechanical characteristic of cortical bone as parameter but two groups samples which best mechanical properties showed an bioactivity progress by apatite deposition. The conclusions of this study can be stated that there’s none of group sample can be applied as implant plate materials but nanocomposite metakaolin-strontium doped carbonate apatite and chitosan as coupling agent for implant plate with a mass ratio 2:1 has the most optimum characteristic and showed a potential as bone initiator and implant plate for trabecular bone. |
| Kata kunci | Plat implan, metakaolin, karbonat apatit, stronsium, kitosan |
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar Purwasasmita, M. Eng., Ph.D |
| Pembimbing 2 | Dr. drg. A. Haris Budi Widodo, M.Kes., A.P., S.IP |
| Pembimbing 3 | |
| Tahun | 2016 |
| Jumlah Halaman | 21 |
| Tgl. Entri | 2016-04-27 01:46:04.850662 |