| Judul Artikel | PENGARUH VARIASI pH SALIVA BUATAN DAN LAMA WAKTU PERENDAMAN TERHADAP LAJU KOROSI ALLOY Ti-6Al-4V PADA PORCELAIN FUSE TO METAL |
|---|
| Abstrak (Bhs. Indonesia) | Ti-6Al-4V adalah tersusun oleh 90% atom titanium, 6% atom aluminium, 4% atom vanadium dan termasuk dalam klasifikasi panduan titanium yang mempunyai fase alpha-betha..Tujuan penelitian ini adalah untuk mengetahui pengaruh variasi pH saliva buatan dan lama waktu perendaman terhadap laju korosi alloy Ti-6Al-4V pada porcelain fuse to metal.Jumlah total 48 sampel yang terbagi menjadi 3 kelompok. Bentuk sampel persegi berukuran 11 x13 x 1.4 mm.Sampel direndam dengan lama waktu 7, 14, 21 dan 28 hari dengan variasi pH saliva buatan 2,3, 6,8 dan 8,5. Subjek penelitian selanjutnya dilakukan uji atomic absorption spectrophotometry (AAS) untuk melihat pelepasan atom titanium, aluminium dan vanadium. Uji Two- Way ANOVA menunjukkan pelepasan titanium tidak mengalami pelepasan ion secara signifikan (p > 0,005). Hasil uji pelepasan ion aluminium dan vanadium memiliki hasil yang signifikan (p < 0,005). Hasil penelitian menunjukkan adanya pengaruh variasi pH saliva buatan dan lama waktu perendaman terhadap laju korosi alloy Ti-6Al-4V pada porcelain fuse to metal. |
|---|
| Abtrak (Bhs. Inggris) | Ti-6al-4v is composed by 90 % atoms titanium, 6 % atoms aluminum, 4 % atoms vanadium and including in the classification guide titanium in which that have phase alpha-betha. the purpose of this research is to find variations ph saliva artificial and long soaking to the rate corrosion alloy ti-6al-4v in porcelain fuse to metal.jumlah total 48 sample that is divided into three groups of.The form of sample square measuring 11 x13 x 1.4 mm.sampel soaked with long period of seven, 14, 21 and 28 days with variations ph saliva artificial 2.3, 6.8 and 8.5.The subject of study next undergone a atomic absorption spectrophotometry (aas) to watch the release of atoms titanium, aluminum and vanadium.Test two- way anova show the release of titanium did not experience the release of ions significantly (p > 0,005).The results of the discharge ions aluminum and vanadium having results significant (p < 0,005). The result showed the influence of ph saliva artificial and a long time soaking against the corrosion alloy ti-6al-4v on porcelain fuse to metal. |
|---|
| Kata kunci | Saliva buatan, variasi pH, Ti-6al-4V, porcelain fuse to metal, atomic absorption spectrophotometry (AAS) |
|---|
| Pembimbing 1 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 2 | Anung Riapanitra, S.Si, M.Sc |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 20 |
|---|
| Tgl. Entri | 2016-04-06 23:11:14.948881 |
|---|