| Judul Artikel | PERBANDINGAN KEKUATAN TARIK RELINING GIGI TIRUAN NILON TERMOPLASTIK DERAJAT KRISTALIN TINGGI MENGGUNAKAN AKRILIK SELF CURED DENGAN VARIASI SURFACE TREATMENT |
|---|
| Abstrak (Bhs. Indonesia) | Nilon termoplastik sebagai basis gigi tiruan, memiliki beberapa kekurangan antara lain sulitnya dilakukan relining dan sulit melekat dengan resin akrilik self cured. Kombinasi surface treatment dibutuhkan untuk meningkatkan akrilik self cured dengan nilon termoplastik. Tujuan penelitian ini adalah untuk mengamati efek kombinasi surface treatment terhadap perlekatan relining nilon termoplastik kristalin tinggi menggunakan resin akrilik self cured. Jenis penelitian ini merupakan jenis eksperimental laboratoris murni dengan teknik pengambilan sampel yaitu simple random sampling. Sampel berbentuk silinder berjumlah 32 buah dibagi menjadi 4 kelompok sesuai dengan metode surface treatment yang akan diaplikasikan, aplikasi silane (kontrol), kombinasi diklorometana dan silane, kombinasi alumina sandblasting dan silane, kombinasi silica coating dan silane. Seluruh sampel selanjutnya dilakukan prosedur relining menggunakan resin akrilik self cured. Setiap kelompok kemudian direndam pada saliva buatan selama 24 jam. Kekuatan perlekatan diuji menggunakan uji tarik. Hasilnya menunjukan terdapat perbedaan bermakna (p<0,05) untuk kekuatan perlekatan pada kelompok aplikasi silane, kombinasi diklorometana dan silane, kombinasi alumina sandblasting dan silane, serta kombinasi silica coating dan silane. Simpulan penelitian ini adalah kombinasi surface treatment dapat meningkatkan kekuatan tarik relining nilon termoplastik derajat kristalin tinggi menggunakan akrilik self cured dan kelompok silica coating kombinasi silane menunjukan kekuatan tarik tertinggi. Pengembangan penelitian selanjutnya dapat dilakukan uji transversa untuk melihat sifat fisik nilon termoplastik yang telah dilakukan relining menggunakan akrilik self cured setelah diberikan variasi surface treatment.
|
|---|
| Abtrak (Bhs. Inggris) | Nylon thermoplastic as a denture base material have some disadvantage included difficulties in reline and poor adherences to the self cured acrylic resin. A combined surface treatment is necessary to strengthen the bond of self cured acrylic resin to thermoplastic nylon. This study aimed to investigated the effect of combined surface treatment on the bond strength high crystalline nylon thermoplastic material to a self cured acrylic resin. This study is an experimental laboratory research and used simple random sampling technique. The specimens used 32 cylinder nylon thermoplastic were divide into four groups according to the surface treatment method, silane application (control), combination dichloromethane - silane application, alumina sandblasting - silane application, and silica coating - silane application. These four groups were relined with a self cured acrylic resin. The specimens were immersed in artificial saliva for 24hr. Bond strength were determined with a tensile test. The result of tensile test was analyzed by one way ANOVA and LSD post hoc. The result showed that significant differences (p<0,05) for bond strength of silane group, dichloromethane – silane group, alumina sandblasting –silane group, and silica coating –silane group. The conclusion of this research were combined surface treatment could increase the tensile bond strength of high crystalline thermoplastic nylon that relined with self cured acrylic resin and the silica coating - silane combination showed the highest tensile strength. The development of further research can be done by transverse test to evaluation physic strength relined thermoplastic nylon with self cured acrylic resin after treated with variations of surface treatment. |
|---|
| Kata kunci | Nilon termoplastik, relining, akrilik self cured, silica coating, alumina sandblasting, silane, kekuatan tarik |
|---|
| Pembimbing 1 | drg. Rinawati Satrio,M.Si |
|---|
| Pembimbing 2 | drg. Setiadi W. Logamarta, Sp.Ort |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 21 |
|---|
| Tgl. Entri | 2016-02-20 13:23:43.489358 |
|---|