| Judul Artikel | PERBANDINGAN KEKUATAN GESER PERLEKATAN PASAK GLASS FIBER DENGAN RESIN KOMPOSIT CORE BUILD UP MENGGUNAKAN VARIASI KONSENTRASI SILANE |
|---|
| Abstrak (Bhs. Indonesia) | Pasak prefabricated jenis glass fiber dan resin komposit core build up menjadi pilihan pasca perawatan saluran akar. Bahan surface treatment yang digunakan pada permukaan pasak glass fiber adalah hidrogen peroksida 24%. Perlekatan antara pasak glass fiber dengan resin komposit core build up dapat ditingkatkan dengan pemberian silane. Silane yang saat ini ada dipasaran terdapat dalam konsentrasi 1%, 2,5% dan 5% dengan jenis γ-methacryloxypropyl-trimethosilane (MPS). Tujuan dari penelitian ini adalah untuk mengetahui perbandingan kekuatan geser perlekatan pasak glass fiber dengan resin komposit core build up menggunakan variasi konsentrasi silane. Jenis penelitian ini merupakan eksperimental laboratoris yang menggunakan 32 buah sampel, teknik pangambilan sampel dilakukan dengan cara simple random sampling. Sampel penelitian terbagi menjadi 4 kelompok. Kelompok 1 tanpa aplikasi silane, kelompok 2 dengan silane MPS 1%, kelompok 3 dengan silane MPS 2,5% dan kelompok 4 dengan silane MPS 5%. Uji geser dilakukan menggunakan alat Universal Testing Machine. Hasil uji geser dianalisis menggunakan one way ANOVA dan LSD. Hasilnya menunjukkan adanya perbedaan bermakna (p<0,05) pada semua kelompok. Simpulan penelitian ini adalah silane MPS 5% menghasilkan kekuatan geser perlekatan yang lebih tinggi daripada MPS 1% dan MPS 2,5%. Pada penelitian selanjutnya diharapkan dilakukan pengontrolan volume silane yang diaplikasikan ke permukaan pasak glass fiber. |
|---|
| Abtrak (Bhs. Inggris) | Prefabricated glass fiber post and core build up composite resin become the option after root canal treatment. Surface treatment material which used in the surface of glass fiber post is 24% hydrogen peroxide. Silane has the ability to improve bond strength between glass fiber post and composite resin. The aim of this study is to compare shear bond strength of glass fiber with core build up composite resin using different variation of silane concentration. Generally, silane was available in concentration 1%, 2,5% and 5% with type γ-methacryloxypropyl-trimethosilane (MPS). This study was an experimental laboratory which used 32 samples, simple random sampling technique was used in this research. Samples classified into 4 groups, i.e., group 1 was no silanization, group 2 with 1% MPS silane concentration, group 3 with 2,5% MPS silane concentration and group 4 with 5% MPS silane concentration. The shear bond strength tested using Universal Testing Machine. The result of shear bond strength was analyzed in one way ANOVA and LSD. The result reveal that there were significant differences (p<0,05) in all groups. In conclusion, 5% MPS silane concentration produces higher shear bond strength than 1% and 2,5% MPS silane concentration. The study suggest for further research to control silane volume which applied in surface of glass fiber post. |
|---|
| Kata kunci | Pasak glass fiber, resin komposit core build up, silane, kekuatan geser perlekatan |
|---|
| Pembimbing 1 | drg. Sertiadi Warata Logamarta, Sp.Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2016-02-10 14:49:13.980811 |
|---|