| Judul Artikel | KARAKTERISASI SIFAT LISTRIK DAN SIFAT OPTIK LAPISAN TIPIS ZnO:CNT DOPING DYE BUAH NAGA SEBAGAI SENSITIZER SOLAR SEL |
|---|
| Abstrak (Bhs. Indonesia) | Karakterisasi sifat listrik dan sifat optik lapisan tipis ZnO:CNT doping dye buah naga sebagai sensitizer solar sel telah dilakukan. Karakterisasi spektrum transmisi optik dilakukan menggunakan FTIR yang menghasilkan transmitansi setiap sampelnya yaitu SN_0 (0.01-0.7)%, SN_1 (0.3-0.8)%, SN_2 (0.4-0.7)%, SN_3 (0.3-0.9)%, dan SN_4 (0.2-0.9)%. Hasil analisis uji XRD dengan menghasilkan struktur kristal yang terorientasi pada sudut 2θ = 31.77⁰ untuk SN_0, 2θ = 34.48⁰ untuk SN_1, dan 2θ = 34.41⁰ untuk SN_2 dan menggunakan persamaan Scherrer ukuran partikel yang terbentuk 6.90-100.96 nm (SN_0), 81.41-100.96 nm (SN_1), dan 8.41-80.75 nm (SN_2). Hasil pengujian sampel dengan SEM terlihat morfologi ZnO:CNT:dye buah naga 75% yang bercampur secara homogen. Sedangkan untuk uji listrik sel surya menghasilkan arus, tegangan, daya, dan efisiensi. Sampel SN_1 Voc = 289 mV, Isc = 0.8 μA, Vmax = 2 mV, Imax = 0.4 μA, Pmax = 0.6 mW, dan η = 0.0003 %. Sampel SN_2 Voc = 236.35 mV, Isc = 0.5 μA, Vmax = 3 mV, Imax = 0.3 μA, Pmax = 1 mW, dan η = 0.0005 %. Dari hasil yang diperoleh, dapat disimpulkan bawah dye buah naga dapat digunakan sebagai sensitizer.
|
|---|
| Abtrak (Bhs. Inggris) | Characterization the electrical and optical thin film properties of ZnO:CNT doping dragon fruit as a sensitizer solar cell have been made. The experiment were observed by several characterization. Optic spectrum transmision characterization by FTIR, The measurement revealed that each transmision produce SN0 (0.01-0.7)%, SN1 (0.3-0.8)%, SN2 (0.4-0.7)%, SN3 (0.3-0.9)% and SN4 (0.2-0.9)%. The x-ray diffraction characterization determine the crystal structure, oriented at 2θ = 31.77⁰ (SN0), 34.48⁰ (SN1), 34.41⁰ (SN2). Based on Scherrer equation, the particle size have a range 6.90-100.96 nm (〖SN〗_0), 81.41-100.96 nm (〖SN〗_1), dan 8.41-80.75 nm (〖SN〗_2). The morfology were observed by SEM revealed that 75% ZnO:CNT:dye dragon fruit 75% was homogen. Meanwhile, the electrical properties of solar cell produce the current, voltage, power and eficiency. Respectively, SN1 Voc = 289 mV, Isc = 0.8 μA, Vmax = 2 mV, Imax = 0.4 μA, Pmax = 0.6 mW, dan η = 0.0003 %. SN2 Voc = 236,35 mV, Isc = 0.5 μA, Vmax = 3 mV, Imax = 0.3 μA, Pmax = 1 mW, dan η = 0.0005 %. The experiment revealed that dye dragon fruit be able as alternative to be a sensitizer.
|
|---|
| Kata kunci | Kata Kunci : DSSC, Buah Naga, ZnO, CNT, dye |
|---|
| Pembimbing 1 | Kartika Sari, M.Si |
|---|
| Pembimbing 2 | Drs. Sunardi, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 5 |
|---|
| Tgl. Entri | 2016-02-05 13:40:43.702831 |
|---|