| Judul Artikel | PERBANDINGAN TINGKAT PENYERAPAN FLUOR ANTARA GLASS IONOMER CEMENT TIPE VIII DAN COMPOMER DALAM OBAT KUMUR FLUORIDE |
|---|
| Abstrak (Bhs. Indonesia) | Karies gigi merupakan suatu hasil fermentasi karbohidrat oleh bakteri menjadi asam sehingga terjadi demineralisasi pada jaringan keras gigi, namun terjadinya karies gigi ini dapat dicegah dengan menggunakan fluoride. Kandungan fluoride dapat ditemukan pada bahan restorasi glass ionomer cement dan compomer. Kedua bahan restorasi tersebut mampu menyerap fluoride dari lingkungannya seperti obat kumur. Penelitian ini bertujuan untuk mengetahui perbandingan tingkat penyerapan fluoride antara glass ionomer cement tipe VIII dan compomer dalam obat kumur fluoride. Jenis penelitian ini merupakan penelitian eksperimental laboratoris dengan membagi sampel menjadi dua kelompok, yaitu kelompok glass ionomer cement tipe VIII dan kelompok compomer. Masing-masing kelompok diuji pre-test dan post test. Hasil uji penyerapan fluoride menggunakan EDS diuji menggunakan uji saphiro-wilk, levene test, paired t-test, kemudian diuji menggunakan independent t-test. Hasilnya menunjukkan terdapat perbedaan bermakna dimana jumlah penyerapan fluoride pada kelompok glass ionomer cement tipe VIII lebih tinggi dibandingkan dengan kelompok compomer. Hasil uji karakteristik morfologi mikrostruktur dengan SEM menunjukkan kelompok glass ionomer cement tipe VIII memiliki ukuran celah dan porus yang lebih besar serta lebih banyak dibanding kelompok compomer. Simpulan penelitian ini adalah glass ionomer cement memiliki kemampuan penyerapan fluoride yang lebih tinggi dibanding dengan compomer karena GIC tipe VIII memiliki porus yang lebih banyak dan lebih besar dibanding compomer, sehingga GIC tipe VIII lebih optimal digunakan dalam pencegahan karies primer maupun sekunder. |
|---|
| Abtrak (Bhs. Inggris) | Dental caries is a result of carbohydrate fermentation by bacteria into acids causing demineralization in hard tissue of teeth, but dental caries can be prevented with the use of fluoride. The content of fluoride can be found on the restorative material of glass ionomer cement and compomer. Both restorative materials are able to absorb fluoride from the environment such as mouthwash. This study aimed to compare the absorption rate of fluoride between glass ionomer cement types VIII and compomer in fluoride mouthwash. This type of research is an experimental research laboratory by dividing the sample into two groups, namely the glass ionomer cement types VIII and compomer. Each group had pre-test and post-test. The test result of fluoride using EDS was tested using the shapiro-wilk, levene test, paired t-test. Then it was tested using independent t- test. The results showed there was a significant difference in which the amount of absorption of fluoride in glass ionomer cement type VIII was higher than that of compomer. The result of morphological characteristics microstructure by SEM showed glass ionomer cement type VIII had a bigger size of cracks and porous more than those of compomer. The conclusions of this study is glass ionomer cement has the ability absorption of fluoride higher than the compomers GIC-type VIII has more and larger porous than the compomer. Therefore, GIC-type VIII is more optimal to be used in primary and secondary caries prevention. |
|---|
| Kata kunci | Karies gigi, glass ionomer cement, compomer, obat kumur, penyerapan fluoride, SEM, EDS |
|---|
| Pembimbing 1 | drg.Setiadi W. Logamarta, Sp.Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 18 |
|---|
| Tgl. Entri | 2016-01-26 20:26:53.266406 |
|---|