| Judul Artikel | PENGARUH KATALIS ALUMINIUM OKSIDA PADA DEGRADASI POLIETILEN TEREFTALAT (PET) DENGAN METODE GLIKOLISIS |
|---|
| Abstrak (Bhs. Indonesia) | PET (Polietilen Tereftalat) merupakan salah satu jenis plastik yang sering digunakan dalam kehidupan sehari-hari, khususnya digunakan dalam kemasan minuman. Meningkatnya penggunaan PET menyebabkan jumlah limbah PET meningkat dengan cepat setiap tahunnya. Oleh karena itu, diperlukan daur ulang limbah PET melalui proses degradasi dengan menggunakan katalis aluminium oksida dan mengguunakan metode glikolisis. Proses degradasi PET pada penelitian ini dimulai dengan preparasi sampel. Selanjutnya proses degradasi dilakukan dengan proses refluks menggunakan pelarut etilen glikol dan katalis aluminium oksida dengan variasi 0; 0,3; 0,6; dan 0,9 g. Hasil degradasi dikarakterisasi titik leleh, spektrum FTIR, dan XRD. Hasil penelitian menunjukkan bahwa, titik leleh sampel berubah menjadi jauh lebih rendah dibandingkan dengan sebelum degradasi. Titik leleh sampel yang paling rendah yaitu mencapai 100 oC. Katalis aluminium oksida yang digunakan dalam penelitian mempengaruhi produk hasil glikolisis, yaitu titik leleh produk semakin mendekati 109 oC. |
|---|
| Abtrak (Bhs. Inggris) | PET (Polyethylene Terephthalate) is one type of plastic that is often used in everyday life, especially used in packaging beverages. The increasing use of PET causes the amount of PET waste is increasing rapidly every year. Therefore, it is necessary PET waste recycling through the degradation process by using aluminum oxide catalysts and methods of glycolysis. PET degradation process in this study begins with sample preparation. Furthermore, the degradation process carried out by refluxing process using solvent ethylene glycol and aluminum oxide catalyst with variation 0; 0.3; 0.6; and 0.9 g. Characterized degradation products melting point, FTIR spectrum and XRD. The results showed that, the melting point of the sample turns into much lower compared with before degradation. The melting point of the lowest sample is 100 oC. Aluminum oxide catalyst used in the study affect the product of glycolysis, which is the melting point of the product is getting closer to 109 oC. |
|---|
| Kata kunci | Kata kunci: Aluminium oksida, degradasi, depolimerisasi, glikolisis, polietilen tereflatat (PET) |
|---|
| Pembimbing 1 | Dra. Eva Vaulina Y. D., M.Si. |
|---|
| Pembimbing 2 | Ely Setiawan, M.Si. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2016 |
|---|
| Jumlah Halaman | 12 |
|---|
| Tgl. Entri | 2016-01-19 04:40:14.888193 |
|---|