| Judul Artikel | PENGARUH VARIASI UKURAN PARTIKEL BAMBU DAN JUMLAH SEMEN PERBANDINGAN CAMPURAN SERAT AREN 0%, 50%, DAN 100% TERHADAP SIFAT FISIKA DAN MEKANIKA BALOK SEMEN |
|---|
| Abstrak (Bhs. Indonesia) | Seiring meningkatnya kebutuhan manusia terutama dibidang konstruksi mengakibatkan berkurangnya ketersediaan kayu. Tujuan dari penelitian ini untuk mengetahui sifat fisika dan mekanika balok semen. Bahan yang dapat digunakan sebagi alternatif pengganti kayu yaitu limbah serutan bambu dan serat aren diolah menjadi produk komposit berupa balok semen. Penelitian ini bertujuan untuk mengetahui sifat fisika dan mekanika balok semen. Penelitian ini menggunakan rancangan acak dengan percobaan 3 faktorial yaitu faktor semen ( 1 bahan : 2 semen, 1: 3, 1:4), faktor ukuran partikel (1cm x 1cm tertahan 0,5cm x 0,5cm, 0,5cm x 0,5 tertahan 0,2cm x 0,2cm, 0,2cm tertahan 0,1cm x 0,1cm) dan kadar partikel bambu : serat aren (100% : 0%, 50% : 50%, 0% : 100%). hasil analisis varian yang berbeda kemudian di uji sifat fisika dan mekanika. Parameter uang diuji pada penelitian ini berdasarkan Standar ASTM D143 yaitu kadar air, berat jenis, penyerapan air, perubahan dimensi, kuat lentur (MOR) dan modulus elastisitas (MOE). Hasil penelitian menunjukkan nilai optimum dari kadar air yaitu 1,82%, berat jenis yaitu 0,838, perubahan dimensi yaitu 0,215%, penyerapan air yaitu 14,666%, kuat lentur (MOR) yaitu 6,455MPa, modulus elastisitas (MOE) yaitu 26742,889 MPa. |
|---|
| Abtrak (Bhs. Inggris) | For the increasing human needs, especially in the field of construction resulted in reduced availability of wood. The purpose of this study was to determine the physical and mechanical properties of cement blocks. Materials that can be used as an alternative to wood shavings that waste bamboo and palm fiber processed into composite products such as cement blocks. This study uses a randomized complete block design with 3 factorial experiment namely cement factor (1 materials: 2 cement , 1: 3, 1: 4), particle size factor (1cm x 1cm restrained 0,5cm x 0,5cm, 0,5cm x 0, 5 restrained 0,2cm x 0,2cm, 0,2cm 0,1cm x 0,1cm restrained) and bamboo particle levels: palm fibers (100%: 0%, 50%: 50%, 0%: 100%). the results of the different variants analysis is tested in physics and mechanics. Parameter that tested in this study is based on the ASTM D143 standard of the water content, density, water absorption, dimensional change, bending strength (MOR) and modulus of elasticity (MOE). The results showed the optimum value of the water content is 1.82%, a specific gravity that is 0, 838, changes in dimensions is 0.215%, water absorption is 14.666%, bending strength (MOR) is 6,455MPa, modulus of elasticity (MOE), namely 26742,889 MPa. |
|---|
| Kata kunci | Kata kunci : partikel bambu, serat aren, sifat fisika, sifat mekanika |
|---|
| Pembimbing 1 | Dr. Nor Intang, S.H., S.T., M.T. |
|---|
| Pembimbing 2 | Dr. IGL Bagus Eratodi, S.T., M.T. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 11 |
|---|
| Tgl. Entri | 2015-12-30 11:01:07.283535 |
|---|