| Judul Artikel | PERBEDAAN FRACTURE RESISTANCE TEKNIK OPEN DAN CLOSED CENTRIPETAL BUILD-UP DENGAN FLOWABLE BULK FILL SEBAGAI INTERMEDIATE LAYER PADA RESTORASI KELAS II |
|---|
| Abstrak (Bhs. Indonesia) | Kavitas kelas II memiliki sisa struktur gigi yang relatif sedikit serta memiliki nilai C factor besar, yang dapat mempengaruhi ikatan antara struktur gigi dan resin komposit. Penempatan flowable bulk fill dan modifikasi teknik penumpatan, dengan teknik centripetal build-up dapat meminimalkan efek polymerization shrinkage resin komposit. Kombinasi dari dua teknik tersebut memiliki dua percabangan, yaitu open centripetal build-up (OCT) dan closed centripetal build-up (CCT). Tujuan penelitian ini adalah untuk mengetahui besarnya fracture resistance dari kavitas kelas II, yang telah direstorasi dengan teknik OCT dan CCT dengan variasi ketebalan flowable bulk fill. Sebanyak 32 sampel dikelompokkan menjadi 4 kelompok yaitu kelompok 1 kombinasi OCT dan flowable bulk fill 1mm, kelompok 2 kombinasi OCT dan flowable bulk fill 2mm, kelompok 3 kombinasi CCT dan flowable bulk fill 1mm, dan kelompok 4 kombinasi OCT dan flowable bulk fill 2mm. Pengujian dilakukan dengan menggunakan Universal Testing Machine, dengan jig bulat berdiameter 5mm kecepatan 0,5mm/min. Uji ANOVA menunjukkan tidak adanya perbedaan bermakna antara kelompok 1 dan kelompok 2 p=0,202, kelompok 3 dan 4 p=0,414, sedangkan perbedaan bermakna ditunjukkan antara kelompok 1 dan 3 p=0,006, serta kelompok 2 dan 4 p=0,018. Simpulan penelitian ini teknik closed centripetal build-up menghasilkan nilai fracture resistance yang lebih besar daripada teknik open centripetal build-up dan aplikasi flowable bulk fill dengan ketebalan 2 mm juga menghasilkan nilai fracture resistance yang lebih besar daripada ketebalan 1 mm. Pada penelitian selanjutnya diharapkan dapat dilakukan penelitian dengan mengaplikasikan flowable bulk fill yang lebih tebal. |
|---|
| Abtrak (Bhs. Inggris) | In class II cavity, the rest of tooth structure is relatively a bit and it has high C factor, that can influence the bond between tooth structure and composite. The aplication of flowable bulk fill and use centripetal build-up technique, can minimized the effect of polymerization shrinkage of composite. Combination of that technique has two branch, open centripetal build-up (OCT) and closed centripetal build-up (CCT). Aims of this research was to determine the fracture resistance of class II cavity, that has been restored with OCT and CCT technique, with the variation of flowable bulk fill thickness. Total of 32 samples were grouped into 4 groups, group 1 combination of OCT and 1mm flowable bulk fill, group 2 combination of OCT and 2mm flowable bulk fill, group 3 combination of CCT and 1mm flowable bulk fill, and group 4 combination of CCT and 2mm flowable bulk fill. Fracture resistance test was tested by Universal Testing Machine, with 5mm round jig and speed 0,5mm/min. ANOVA showed no significant difference between group 1 and 2 p=0,202, group 3 and 4 p=0,414, whereas significance difference was shown between group 1 and 3 p=0,006, as well as group 2 and 4 p=0,018. Based on data analysis can be concluded that closed centripetal build-up has better fracture resistance value than open centripetal build-up technique and 2 mm flowable bulk fill thickness has better fracture resistance value than 1 mm flowable bulk fill thickness. In subsequent research is expected to be carried out the aplication of thicker flowable bulk fill. |
|---|
| Kata kunci | Fracture resistance, ketebalan flowable bulk fill, closed centripetal build-up, open centripetal build-up |
|---|
| Pembimbing 1 | drg. Setiadi W. Logamarta, Sp.Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 19 |
|---|
| Tgl. Entri | 2015-12-23 07:15:16.952868 |
|---|