| NIM | G1G010040 |
|---|
| Namamhs | CITA CHUSNUL CHOTIMAH |
|---|
| Judul Artikel | PERBEDAAN KEKUATAN GESER BRAKET METAL PADA RESTORASI RESIN MODIFIED GLASS IONOMER CEMENT DAN RESIN KOMPOSIT LIGHT CURED MENGGUNAKAN BONDING KOMPOSIT LIGHT CURED |
|---|
| Abstrak (Bhs. Indonesia) | Ortodontis seringkali mendapatkan pasien dengan kondisi gigi yang telah direstorasi, salah satu restorasi yang erat kaitannya dengan adanya braket yaitu restorasi yang terletak di permukaan labial dan bukal gigi. Permukaan restorasi yang halus menyebabkan resin komposit ortodontik tidak dapat penetrasi secara sempurna sehingga menyebabkan kekuatan perlekatan braket yang cenderung lemah atau terjadi kegagalan perlekatan bonding braket. Penelitian ini bertujuan untuk mengetahui perbedaan kekuatan geser braket metal pada restorasi RMGIC dan resin komposit light cured menggunakan bonding komposit light cured. Jenis penelitian ini adalah eksperimental laboratorium murni dengan metode post test-only control group design. Bahan adhesif yang digunakan adalah resin komposit ortodontik light cured. Braket yang digunakan adalah standar edgewise untuk gigi premolar pertama rahang atas dengan permukaan mesh base. Sebanyak 27 sampel dibagi menjadi 3 kelompok. Kelompok 1 sebagai kelompok kontrol yaitu braket metal pada gigi tanpa restorasi, kelompok 2 sebagai kelompok perlakuan yaitu braket metal pada permukaan RMGIC, dan kelompok 3 sebagai kelompok perlakuan yaitu braket metal pada permukaan resin komposit restoratif. Uji kekuatan geser dilakukan dengan alat Torsee’s Digital System Universal Testing Machine. Uji ANOVA menunjukkan adanya perbedaan yang bermakna antara tiga kelompok. Kelompok 1 memiliki rerata kekuatan geser tertinggi (14,52 MPa), selanjutnya kelompok 3 (5,85 MPa) dan kelompok 2 (3,39 MPa). Kelompok 1 memiliki perbedaan yang signifikan dengan kelompok 2 dan 3, serta kelompok 2 memiliki perbedaan yang signifikan dengan kelompok 3. Jenis fraktur yang paling banyak terjadi pada penelitian ini adalah adhesive failure in sample surface yaitu sebanyak 17 sampel dari total 27 sampel. Simpulan penelitian ini yaitu terdapat perbedaan kekuatan geser braket metal pada restorasi resin modified glass ionomer cement dan resin komposit light cured menggunakan bonding komposit light cured. Saran yang dapat diberikan adalah pembuatan sampel menggunakan RMGIC dalam bentuk capsulated, agar homogenitas tiap sampel lebih merata dan kemungkinan adanya variasi antar sampel dapat diminimalkan. |
|---|
| Abtrak (Bhs. Inggris) | Orthodontist often get patients with the condition of a tooth that has restored, one restoration that were closely related with the bracket is the restoration lies on the surface labial or buccal teeth. The restoration surface is rather smooth, which caused the orthodontic composite resin failed to penetrate perfectly, which lead to the low shear bond strength of othodontic bracket. This study was aimed to determine the shear bond strength difference between orthodontic metal bracket to restorative resin modified glass ionomer cement and light cured composite resin surface. This study was a pure experimental laboratory study, with post test only control group design. Orthodontic light cured composite was used for adhesive material. Edgewise standard bracket with mesh base for first premolar was used in this study. 27 first maxillary human premolars were randomly divided into three groups. In Group 1/Control Group, the metal brackets were bonded to teeth without restoration. In Group 2 and 3, as the treatment group, the metal brackets were bonded to teeth with RMGIC and restorative composite restoration, respectively. The shear bond strength was determined with Torsee’s Digital Universal Testing Machine. ANOVA revealed that there was significant difference between the three groups. The highest shear bond strength was found in Group 1 (14,52 MPa), followed by Group 3 (5,85 MPa) and Group 2 (3,39 MPa). There were significant differences between Group 1 and 2, Group 1 and 3. The significant difference was also found in Group 2 and 3. The type of fracture that mostly happens in this research is adhesive failure in sample surface with 17 sample of the total 27 sample. The conclusion of this research is there is a difference between shear bond strength orthodontic bracket to restorative resin modified glass ionomer cement and light cured composite resin surface with light cured composite BONDING. For upcoming study, it was suggested to use the capsulated-form of RMGIC sample to obtain the homogenity between sample and minimize the variaton. |
|---|
| Kata kunci | Resin modified glass ionomer cement, resin komposit light cured, uji geser |
|---|
| Pembimbing 1 | drg. Setiadi W. Logamarta, Sp. Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M. Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 16 |
|---|
| Tgl. Entri | 2015-11-23 17:03:56.263338 |
|---|