| Judul Artikel | PENGARUH VARIASI LAMA INKUBASI TERHADAP PERLEKATAN Candida albicans DAN MODULUS ELASTISITAS BASIS GIGITIRUAN NILON TERMOPLASTIK DERAJAT KRISTALIN TINGGI DENGAN PELAPIS NANOPARTIKEL PERAK
|
|---|
| Abstrak (Bhs. Indonesia) | Permukaan basis gigitiruan yang kasar dapat menyebabkan kolonisasi mikroba pada basis gigitiruan. Salah satu jenis mikroba yang dapat tumbuh yaitu Candida albicans. Aplikasi bahan pelapis nanopartikel perak pada permukaan basis gigitiruan dapat menurunkan perlekatan C. albicans, namun modifikasi pada basis gigitiruan tersebut dapat mempengaruhi sifat mekanis dari basis gigitiruan. Penelitian ini bertujuan untuk mengetahui pengaruh pelapis nanopartikel perak terhadap perlekatan C. albicans dan modulus elastisitas basis gigitiruan nilon termoplastik derajat kristalin tinggi. Jenis penelitian ini adalah eksperimental dengan menggunakan 32 sampel nilon termoplastik derajat kristalin tinggi yang dibagi secara acak menjadi 8. Kelompok kontrol tidak diberikan pelapis nanopartikel perak, sedangkan kelompok perlakuan diberikan pelapis nanopartikel perak. Setiap kelompok direndam dalam suspensi C. albicans dan di inkubasi selama 1 jam, 3 jam, 8 jam dan 12 jam dengan suhu 370C. Setiap waktu inkubasi terdiri atas 4 sampel. kemudian seluruh sampel ditanam dalam media SDA dan jumlah koloni dihitung dengan alat colony counter. Uji modulus elastisitas dilakukan dengan alat Torsee’s Electronic System Universal Testing Machine. Uji one way ANOVA menunjukkan bahwa terdapat perbedaan signifikan antara jumlah perlekatan C. albicans pada kelompok kontrol dan kelompok perlakuan dengan p = 0,000 (p<0,05). Uji Independent T-Test menunjukkan bahwa tidak terdapat perbedaan signifikan pada modulus elastisitas antara kedua kelompok dengan p = 0,769. Aplikasi bahan pelapis nanopartikel perak pada permukaan basis gigitiruan nilon termoplastik derajat kristalin tinggi dapat menurunkan perlekatan C. albicans tanpa menurunkan modulus elastisitas. |
|---|
| Abtrak (Bhs. Inggris) | Rough denture base surface can cause colonization of microorganisms on the denture. Candida albicans is one of microorganism which could grow on the denture. Application silver nanoparticles coating on denture base can decrease C. albicans adherence, however surface modification on denture base can affect mechanical properties of denture base. The aim of this study was to determine the effect of silver nanoparticles coating on C. albicans adherence and modulus elasticity of high crystalline degree nylon thermoplastic denture base. This study was an experimental laboratory research using 32 samples of high crystalline degree nylon thermoplastic denture base that were randomly divided into 8 groups: treatment groups (applied by silver nanoparticles coating) and control group (without any treatment). Each sample was immersed in yeast suspension and incubated at 37oC for 1, 3, 8, 12 hours. Four samples were used for each incubation time. Each sample then was inoculated on SDA medium and colony amount was counted by colony counter. Modulus elasticity test was determined with Torsee’s Electronic System Universal Testing Machine. One Way ANOVA revealed that there were statistically significant differences on C. albicans adherence between the treatment and control group p=0,000 (p<0,05). Independent T-Test revealed that no significant differences were found on modulus elasticity between the treatment and control group p=0,769. Application silver nanoparticles coating on high crystalline degree nylon thermoplastic denture base surface could decrease C. albicans adherence without decrease modulus elasticity. |
|---|
| Kata kunci | Nanopartikel perak, nilon termoplastik, perlekatan Candida albicans, modulus elastisitas |
|---|
| Pembimbing 1 | drg. Rinawati Satrio, M.Si. |
|---|
| Pembimbing 2 | Dr. Nuniek Ina Ratnaningtyas, M.S. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 20 |
|---|
| Tgl. Entri | 2015-11-16 09:44:41.790276 |
|---|