| NIM | H1E011046 |
|---|
| Namamhs | LESTARI NUGRAHANI |
|---|
| Judul Artikel | STRUKTUR, SIFAT MAGNETIK DAN ABSORPSI GELOMBANG MIKRO MANGANESE FERRITE DENGAN DOPING ZnO
|
|---|
| Abstrak (Bhs. Indonesia) | Pembuatan manganese zinc ferrite dilakukan dengan metode reaksi padatan dengan komposisi Mn(1-x)Zn(x)Fe2O3 dimana x = 0; 0,1; 0,3 (mol). Bahan baku yang digunakan adalah Fe2O3 yang diperoleh dari Fe3O4 alam, ZnO (Aldrich, kemurnian 99,9%) dan MnO2 (acros organics, kemurnian 99,9%). Metode reaksi padatan terdiri dari proses pencampuran kemudian pemadatan dan sintering pada suhu 1100˚C selama 3 jam. Karakterisasi XRD, VSM dan VNA dilakukan untuk menganalisis struktur kristal, sifat magnetik serta penyerapan gelombang mikro. Hasil karakterisasi menunjukkan bahwa terlihat sebagian besar fasa manganese zinc ferrite. Sementara itu nilai magnetisasi remanen (Mr) dan magnetisasi saturasi (Ms) menurun pada sampel variasi 0,1 ke sampel variai 0,3 tetapi medan koersivitas (Hc) meningkat. Pada sampel pertama dengan variasi x=0 memiliki Mr dan Ms sangat kecil hal ini dikarenakan terlalu banyak komposisi dari unsur MnO2 yang memiliki sifat paramagnetik. Penyerapan gelombang mikro tertinggi yaitu ada pada sampel dengan variasi x= 0,3 yaitu pada frekuensi diantara 7 – 9 GHz. Secara umum, penambahan ZnO hanya berpengaruh terhadap besar kecilnya nilai reflection loss, tetapi tidak berpengaruh terhadap lebar pita frekuensi pada material tersebut. Material magnetik ini sangat menjanjikan untuk aplikasi-aplikasi absorpsi gelombang mikro. |
|---|
| Abtrak (Bhs. Inggris) | Manganese zinc ferrites are synthesized using solid state reactions, with composition of Mn(1-x)Zn(x)Fe2O3 where x =0; 0.1; 0.3 (mol). Fe2O3 derived from natural Fe3O4, ZnO (Aldrich, purity 99,9%) and MnO2(acros organics, purity 99,9%) are used as raw materials. Solid state reactions method consist of mixing process, compaction and sintering at 1100 ˚C for 3 hours. XRD, VSM and VNA characterizations are conducted in order to analyze structure, magnetic properties and microwave absorption. The results show that the sample is dominated by manganese zinc ferrite phases. Meanwhile, remanent magnetization (Mr) and saturation magnetization (Ms) of the sample with x= 0.1 and 0.3 decrease but the coersivity magnetization (Hc) increases. Sampel, with concentration x = 0 has Mr and Ms lower than other because there’s too much MnO2 which has paramagnetic properties. The highest microwave absorption is showed by sample with variation x = 0.3 in frequency range between frequency 7 – 9 GHz. Generally, the addition of ZnO concentration only affects to the reflection loss value, but do not affect to frequency band of the sample. This magnetic material is very promosing for microwave absorption applications. |
|---|
| Kata kunci | manganese zinc ferrite, Fe3O4 alam, reaksi padatan, struktur, sifat magnetik, absorpsi gelombang mikro. |
|---|
| Pembimbing 1 | Dr. -Ing Wahyu Widanarto |
|---|
| Pembimbing 2 | Wahyu Tri Cahyanto, Ph.D |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 56 |
|---|
| Tgl. Entri | 2015-11-15 21:46:32.058338 |
|---|