| NIM | G1G011027 |
|---|
| Namamhs | ANINDA KARTIKA DEWI |
|---|
| Judul Artikel | KARAKTERISTIK NANOKOMPOSIT METAKAOLIN ZIRKONIA HASIL SINTESTIS DENGAN TEMPLATE TAPIOKA DAN COUPLING AGENT KITOSAN UNTUK MATERIAL RESTORASI GIGI
|
|---|
| Abstrak (Bhs. Indonesia) | Komposit adalah salah satu material restorasi gigi direk yang tersusun dari tiga komponen utama yaitu matriks, filler, dan coupling agent. Saat ini banyak dikembangkan filler dengan ukuran nano yang disebut nanokomposit. Bahan yang berasal dari alam seperti metakaolin, zirkonia, tapioka, dan kitosan merupakan salah satu alternatif yang berpotensi sebagai material restorasi gigi. Tujuan penelitian ini adalah mengetahui karakteristik nanokomposit metakaolin zirkonia dengan penambahan template tapioka 0,4% v/v, 0,8% v/v, 1,6% v/v dan coupling agent kitosan. Metode penelitian yang digunakan adalah eksperimental laboratoris murni. Pembuatan sampel diawali dengan mensintesis metakaolin, zirkonia, dan penambahan template tapioka 0,4% v/v, 0,8% v/v, dan 1,6% v/v yang dibagi menjadi tiga kelompok, kemudian ketiga powder tersebut dicampurkan dengan kitosan sebagai coupling agent. Karakteristik nanokomposit dengan variasi penambahan tapioka sebagai template kemudian dievaluasi dari mikrostruktur dan kekerasan komposit. Hasil SEM dari ketiga sampel menunjukkan ukuran partikel rata-rata 100nm yang mengindikasikan ukuran tersebut telah memenuhi syarat untuk restorasi gigi yaitu sebesar 5-100nm. Hasil uji kekerasan pada sampel A: 36,83 VHN, sampel B: 32,44 VHN, dan sampel C: 40,01 VHN. Simpulan dari penelitian ini adalah sintesis nanokomposit metakaolin zirkonia dengan penambahan template tapioka berhasil dibuat dan memiliki nilai kekerasan rata-rata telah memenuhi nilai kekerasan restorasi komposit untuk gigi dengan nilai kekerasan tertinggi pada sampel C yang memiliki perlekatan dengan gigi paling baik. |
|---|
| Abtrak (Bhs. Inggris) | Composite is one of direct dental restoration material which is consisted of three main components such as matrix, filler, and coupling agent. Nowadays, there're many fillers that is developed in nano size, called nanocomposite. Ingredients derived from nature such as metakaolin, zirconia, tapioca, and chitosan are one of potential alternative as dental restoration material. The purpose of this study is to determine the characteristics of nanocomposite metakaolin zirconia nanocomposite synthetized with the addition of tapioca template variation of 0,4% v/v, 0,8% v/v, 1,6% v/v and chitosan as coupling agent. The study was pure experimental laboratory. The sample was made by synthetizing metakaolin, zirconia, and the addition of tapioca template 0,4% v/v, 0,8% v/v, and 1,6% v/v which were grouped into three, then the three powders were mixed with chitosan as coupling agent. Nanocomposite's characteristics with variations of the addition of tapioca template was then evaluated for its composite microstructure and hardness. The SEM result of the three samples shown a mean particle size of 100nm which indicated that the size was already suitable for dental restoration with value of 5-100nm. The hardness test were as follow, sample A: 36,83 VHN, sample B: 3,44 VHN, and sample C: 40,01 VHN. In this study, the making of nanocomposite metakaolin zirconia with the addition of tapioca template was successful and had mean hardness value which had met the hardness value used for dental composite restoration with the highest hardness value in the sample C which also had the best attachment to the teeth. |
|---|
| Kata kunci | Template tapioka, metakaolin, zirkonia, kitosan, mikrostruktur, kekerasan, restorasi gigi |
|---|
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar P., M.Eng |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 17 |
|---|