| Judul Artikel | KARAKTERISTIK DAN SIFAT ANTIBAKTERI Staphylococcus aureus PADA SCAFFOLD BERBASIS MEMBRAN TELUR BEBEK DENGAN KARBONAT APATIT DAN SENYAWA AKTIF MANGOSTIN UNTUK APLIKASI BONE REPLACEMENT |
| Abstrak (Bhs. Indonesia) | Kasus kerusakan jaringan dapat disebabkan oleh penyakit periodontitis, pencabutan yang menyebabkan fraktur, serta tumor pada rahang. Pemulihan dapat dilakukan dengan transplantasi, tetapi pasca transplantasi sering kali melibatkan berbagai bakteri. Saat ini, berbagai material dikembangkan untuk memperoleh karakteristik optimal pada penggunaan transplantasi, salah satunya adalah scaffold. Scaffold menjadi alternatif yang baik karena dapat dimodifikasi untuk memperoleh sifat biokompatibel, biodegradasi, kekuatan mekanik yang cukup, serta struktur pori yang adekuat. Scaffold disintesis dengan basis membran telur bebek, bahan bioaktif karbonat apatit, bahan antibakteri mangostin dan kitosan serta alginat sebagai pengikat bahan bioaktif, kemudian dipaparkan dalam larutan SBF sebagai lingkungan untuk menguji biokompatibilitas dan biodegradasi. Penelitian dilakukan berdasarkan eksperimental laboratoris murni dengan jumlah spesimen sebanyak 4 kelompok, yaitu membran telur bebek yang direndam dalam larutan alginat, kitosan, karbonat apatit, dan mangostin (A), membran A yang kemudian direndam dalam SBF selama 7 hari (B), 14 hari (C), dan 21 hari (D). Ukuran pori membran berkisar 20 µm hingga 50 µm dan tidak dipengaruhi senyawa perendam. Pengujian FTIR menunjukkan serapan oleh gugus fungsi amina, amida, karboksilat, dan fosfat, sesuai dengan gugus fungsi pada senyawa yang digunakan. Pengujian antibakteri menunjukkan adanya penurunan jumlah koloni Staphylococcus aureus dari 17,5x1014 CFU/mL pada kontrol menjadi 4x1014 CFU/mL pada sampel A, 54x108 CFU/mL pada sampel B, 34x108 CFU/mL pada sampel C, dan 9x108 CFU/mL pada sampel D. Sampel D menunjukkan daya hambat bakteri yang paling besar, yaitu perendaman membran di dalam larutan SBF selama 21 hari. |
| Abtrak (Bhs. Inggris) | The case of tissue damage can be caused by the periodontal disease, extraction causing facture, as well as tumor in jaw. The recovery can be done by transplantation, but post transplantation often involves various bacteria. Nowadays, various bacteria are developed to get optimum characteristics in the transplantation use, one of which is scaffold. Scaffold is the good alternative because it can be modified to obtain the natures of biocompatible, biodegradation, enough mechanic strength, as well as adequate porous structure. Scaffold is synthesized by duck egg membrane based, bioactive material of carbonate appetite, mangostin anti bacterial material and cytosine as well as alginate as the bioactive material binder, then it is exposed to the SBF solution as the environment to test the biocompatibility and biodegradation. The study is conducted based on pure laboratory experiment with the number of specimen is 4 groups, namely the duck egg membrane is soaked in the solutions of alginate, cytosine, carbonate apatite, and mangostin (A), membrane A then is soaked in SBF for 7 days (B), 14 days (C), and 21 days (D). The size of membrane porous is ranging of 20 µm until 50 µm and is not affected by marinade compounds. The FTIR testing shows the absorption by function groups of amine, amide, carboxylate and phosphate, based on the function groups in the used compound. The anti bacterial testing shows that there is a number of colony decrease of Staphylococcus aureus from 17,5x1014 CFU/mL in control into 4x1014 CFU/mL at the A sample, 54x108 CFU/mL at the B sample, 34x108 CFU/mL at the C sample, and 9x108 CFU/mL at the D sample. The D sample shows the biggest bacteria inhibition, namely the membrane marinade in SBF solution for 21 days. |
| Kata kunci | Scaffold, membran telur bebek, karbonat apatit, mangostin, antibakteri |
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar P., M.Eng |
| Pembimbing 2 | Dr. drg. A. Haris B.W. M.Kes A.P.,SIP |
| Pembimbing 3 | |
| Tahun | 2015 |
| Jumlah Halaman | 89 |
| Tgl. Entri | 2015-11-08 22:55:36.017682 |