| Judul Artikel | PENGARUH TEMPLATE TAPIOKA TERHADAP MIKROKAPSUL SILIKA-CHLORHEXIDINE 2% MELALUI METODE SOL-GEL UNTUK APLIKASI DRUG DELIVERY ROOT CANAL TREATMENT |
| Abstrak (Bhs. Indonesia) | Perawatan saluran akar gigi, saat ini masih banyak mengalami kegagalan. Hal ini disebabkan bakteri Enterococcus faecalis yang berada di saluran akar gigi. Chlorhexidine digluconate 2% merupakan salah satu bahan antibakteri yang bersifat bekterisida. Silika mikrokapsul dapat digunakan sebagai pembawa chlorhexidine digluconate untuk mengoptimalkan penggunaannya. Silika mikrokapsul disintesis dari bahan sodium silikat melalui metode sol-gel dengan penggunaan tapioka sebagai template untuk memodifikasi morfologi silika. Penelitian berupa ekperimental laboratoris murni dengan 4 kelompok sampel, yaitu mikrokapsul silika dengan template tapioka 1% (sampel A), mikrokapsul silika dengan template tapioka 2% (sampel B), mikrokapsul silika dengan template tapioka 3% (sampel C), mikrokapsul silika tanpa template tapioka (sampel D). Silika direndam dalam larutan chlorhexidine digluconate 2% agar zat tersebut masuk ke dalam pori, kemudian disalut dengan sodium alginat untuk menutup pori. Gambar SEM menunjukkan sampel B sebagai sampel terbaik karena mikrokapsul silika memiliki ukuran pori partikel 200nm hingga 500nm dengan pori yang homogen. Spektrometri FTIR menunjukkan serapan gugus fungsi yang terkandung dalam silika, kitosan, dan sodium alginat. Spektrometri UV-visible menunjukkan bahwa konsentrasi chlorhexidine digluconate 2% release dari mikrokapsul silika yang disalut dengan sodium alginat dan kitosan sebesar 13,43 ppm setelah 5 menit pertama, 15,40 ppm setelah 5 menit kedua, 17,39 ppm setelah 5 menit ketiga, 18,46 ppm setelah 5 menit keempat, 18,91 ppm setelah 5 menit kelima, dan 19,62 ppm setelah 5 menit keenam. Setelah menit ketiga puluh hingga 1 jam, release chlorhexidine digluconate 2% stabil pada 19,62 ppm. |
| Abtrak (Bhs. Inggris) | There are still many failures in dental root canal treatment. This is caused by the bacterium Enterococcus faecalis in the root canal. Chlorhexidine digluconate 2% is one of the antibacterial with bactericidal property. Silica microcapsules can be used as a carrier to optimize the use of chlorhexidine digluconate. Silica microcapsules were synthesized from sodium silicate through sol-gel method with starch as template to modify the morphology of silica. The research was done as experimental laboratory with four groups of specimens, silica microcapsules synthesized with 1% starch (specimen A), silica microcapsules synthesized with 2% starch (specimen B), silica microcapsules synthesized with 3% starch (specimen C), and silica microcapsules synthesized without starch template (specimen D). Silica microcapsules were soaked in chlorhexidine digluconate 2% solution so that substances get trapped in the pores, and then coated with sodium alginate as pore’s gate. SEM image indicated that specimen B was the best specimen with varying particle pore’s size from 200nm to 500nm with homogeneous pores. FTIR spectrometry resulted the absorptions of functional groups contained in silica, chitosan and sodium alginate. UV-visible spectrometry showed that released concentration of chlorhexidine digluconate 2% from silica microcapsules coated with sodium alginate and chitosan were 13.43 ppm after the first 5 minutes, 15.40 ppm after second 5 minutes, 17.39 ppm after third 5 minutes, 18.46 ppm after fourth 5 minutes, 18.91 ppm after fifth 5 minutes, and 19.62 ppm after sixth 5 minutes. After thirty minutes to 1 hour, released concentration chlorhexidine digluconate 2% was stable at 19.62 ppm. |
| Kata kunci | Mikrokapsul silika, chlorhexidine digluconate 2%, tapioka, kitosan, sodium alginat |
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar Purwasasmita, M.Eng |
| Pembimbing 2 | Dr. drg. A. Haris Budi Widodo, M.Kes, AP, S.IP |
| Pembimbing 3 | |
| Tahun | 2011 |
| Jumlah Halaman | 20 |
| Tgl. Entri | 2015-11-08 14:09:12.781598 |