| Judul Artikel | PERBANDINGAN KARAKTERISTIK ANTARA NANOKOMPOSIT METAKAOLIN-ZIRKONIA-KARBONAT APATIT BERPENGUAT SERAT SELULOSA RANDOM DENGAN DIPILIN UNTUK MATERIAL PASAK GIGI
|
|---|
| Abstrak (Bhs. Indonesia) | Pasak gigi merupakan bagian restorasi yang dimasukkan ke dalam saluran akar gigi nonvital. Salah satu jenis pasak gigi adalah pasak gigi fiber reinforced composite (FRC). Pasak gigi FRC tersusun atas matriks nanokomposit, bonding agent sebagai bahan pengikat, dan serat sebagai bahan penguat. Pengembangan penelitian di bidang biomaterial mendorong penggunaan bahan-bahan kedokteran gigi berbasis alam. Metakaolin, zirkonia, dan karbonat apatit merupakan bahan alam yang dapat digunakan sebagai matriks nanokomposit. Penambahan kitosan sebagai bonding agent dan serat selulosa sebagai penguat, diharapkan dapat meningkatkan sifat mekanik material pasak gigi FRC. Penelitian ini bertujuan untuk mengetahui karakteristik nanokomposit berpenguat serat selulosa, meliputi karakteristik morfologi mikrostuktur, kelenturan, dan kekerasan. Jenis penelitian merupakan penelitian eksperimental laboratoris dengan membagi sampel menjadi enam kelompok, yaitu kelompok A1B1 (serat random 0,1%), A1B2 (serat random 0,3%), A1B3 (serat random 0,5%), A2B1 (serat dipilin 0,1%), A2B2 (serat dipilin 0,3%), dan A2B3 (serat dipilin 0,5%). Hasil karakterisasi morfologi mikrostruktur dengan SEM menunjukkan kelompok A2B3 memiliki ukuran celah paling kecil diantara kelompok yang lain, yaitu sebesar 80μm. Hasil uji flexural dan kekerasan dianalisis menggunakan uji ANOVA, kruskal wallis, LSD, dan mann whitney u test. Hasilnya menunjukkan terdapat perbedaan bermakna untuk nilai flexural strength pada kelompok serat random, nilai flexural strength, dan flexural modulus pada kelompok serat dipilin dengan persentase massa 0,1%; 0,3%; dan 0,5%. Simpulan penelitian ini adalah penambahan serat selulosa sebagai penguat matriks nanokomposit dapat memperkecil ukuran celah dan meningkatkan nilai kelenturan, tetapi tidak mempengaruhi nilai kekerasan. |
|---|
| Abtrak (Bhs. Inggris) | Dental post is a part of restoration which is inserted into a non vital root canal of the tooth. One of the types of dental post is commonly known as fiber reinforced composite (FRC) post. FRC post is composed by nanocomposite matrix, bonding agent as a binding material, and fibers as a reinforcing material. The development of research in the biomaterials’ field, encouraging the use of nature based dental materials. Metakaolin, zirconia, and carbonate apatite are some of natural substances which can be used as a nanocomposite matrix. The addition of chitosan as a bonding agent and the cellulose fibers as a reinforcement, is expected to improve the mechanical properties of the FRC post’s material. This study aims to determine the characteristics of cellulose fibers reinforced nanocomposite, covering the microstructure morphological characteristics, the flexibility, and the hardness. This study is an experimental laboratory research, by dividing the sample into six groups: group A1B1 (random fibers 0.1%), A1B2 (random fibers 0.3%), A1B3 (random fibers 0.5%), A2B1 (twisted fibers 0.1%), A2B2 (twisted fibers 0.3%), and A2B3 (twisted fibers 0.5%). The result of microstructure morphological characterization by SEM shows that group A2B3 has the smallest gap compared to other groups, which is equal to 80μm. The result of flexural test and hardness test was analyzed with ANOVA, kruskal wallis, LSD, and mann whitney u test. The result shows that there were a significant differences in flexural strength’s value of random group, flexural strength’s value of twisted group, and flexural modulus’ value of twisted group with 0.1%, 0.3%, and 0.5% of mass percentage. The conclusions of this study can be stated that the addition of cellulose fiber as a reinforcement of the nanocomposite matrix can reduce the size of the gap and increase the value of flexibility, but has no correlation with the hardness values. |
|---|
| Kata kunci | Pasak gigi, fiber reinforced composite (FRC), serat selulosa, metakaolin, zirkonia, karbonat apatit, kitosan |
|---|
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar Purwasasmita, M. Eng |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M. Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 16 |
|---|
| Tgl. Entri | 2015-11-08 11:43:09.916611 |
|---|