| Judul Artikel | PENURUNAN KADAR LOGAM Cd, Fe, DAN Pb PADA LIMBAH CAIR BATIK MENGGUNAKAN MEMBRAN SELULOSA ASETAT DARI NATA DE BANANA SKIN |
|---|
| Abstrak (Bhs. Indonesia) | Pada penelitian ini telah dilakukan aplikasi membran selulosa asetat dari kulit pisang (nata de banana skin) untuk menurunkan kadar logam kadmium (Cd), besi (Fe), dan timbal (Pb) pada limbah cair batik. Selulosa asetat diperoleh dari proses asetilasi nata de banana skin. Karakterisasi selulosa asetat dilakukan dengan menganalisis gugus fungsi, menentukan berat molekul relatif, dan menentukan kadar asetil. Hasil analisis gugus fungsi dengan menggunakan FTIR menunjukkan adanya serapan khas gugus karbonil (C=O) pada 1738,39 cm-1 dan serapan gugus asetil (C–O) pada 1228,39 cm-1 dengan berat molekul relatif sebesar 6,871x104 g/mol dan kadar asetil sebesar 38,75%. Membran selulosa asetat dibuat dengan teknik inversi fasa. Membran selulosa asetat yang dihasilkan dikarakterisasi dengan mengukur nilai fluks air dan sampel (limbah cair batik) serta diaplikasikan untuk penurunan kadar Cd, Fe, dan Pb. Hasil pengukuran diperoleh nilai fluks air sebesar 6,09 L/(m2.jam) dan fluks limbah sebesar 0,97 L/(m2.jam). Persentase penurunan kadar Cd, Fe, dan Pb dalam limbah cair batik diperoleh masing-masing sebesar 99,46 %, 98,90 %, dan 97,39 %. |
|---|
| Abtrak (Bhs. Inggris) | In this research, cellulose acetate membrane was made from banana peels(nata de banana skin) and then applicated for lowering the level of cadmium (Cd), iron (Fe), and lead (Pb) in the wastewater of batik. Cellulose acetate was obtained by acetylation process of nata de banana skin. Characterization of cellulose acetate is conducted by analyzing the functional groups, determining the molecular weight, and the levels of acetyl. Results of the analysis of functional groups using FTIR showed the absorption of carbonyl group (C = O) in 1738.39 cm-1 and acetyl group (C-O) in 1228.39 cm-1 with a molecular weight of 6.871x104 g/mol and the content of acetyl 38.75%. It was made using phase inversion method. Cellulose acetate membrane also been characterized by measuring the water flux values and sample (wastewater of batik), and it’s application to decreased Cd, Fe, and Pb content in wastewater of batik. The results for water flux value was 6.09 L/(m2.h) and waste flux at 0.97 L/(m2.h). The percentage decrease 99.46 % of Cd content, 98.90 % Fe content, and 97.39 % Pb content in wastewater of batik. |
|---|
| Kata kunci | selulosa asetat, membran selulosa asetat, kadmium (Cd), besi (Fe), timbal (Pb) |
|---|
| Pembimbing 1 | Senny Widyaningsih, M.Si. |
|---|
| Pembimbing 2 | Dian Windy Dwiasi, M.Sc. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 67 |
|---|
| Tgl. Entri | 2015-09-30 18:02:13.172985 |
|---|