| Judul Artikel | Struktur dan Konduktivitas Ionik Kaca LiFePO4 sebagai Katoda pada Baterai Sekunder |
| Abstrak (Bhs. Indonesia) | ABSTRAK Katoda kaca Lithium Iron Phosphates (LiFePO4) telah dibuat dengan menggunakan metode melt-quenching pada temperatur 900 oC dengan komposisi 5Li2O : 15 ZnO : x (Fe2O3) : (80-x) P2O5 dimana x = 0, 0,5, dan 1,5 (mol%). Karakterisasi sifat termal katoda yang meliputi temperatur transisi (Tg) dan temperatur kristal (Tc) dilakukan dengan Differential Scanning Calorimetry (DSC). Pengaruh penambahan Fe2O3 terhadap struktur dan konduktivitas ionik katoda dipelajari dengan X-ray diffraction (XRD) dan LCR meter. Konduktivitas ionik katoda kaca meningkat dengan bertambahnya konsentrasi Fe2O3, namun konduktivitas cenderung menurun pada konsentrasi Fe2O3 yang berlebihan. Nilai konduktivitas ionik dan kapasitas tertinggi katoda sebesar 7,43 x 10-4 S/cm dan 10 x 10-5 Ah/g ditunjukan oleh katoda kaca dengan komposisi Fe2O3 0,5 mol persen. Performa sel baterai LiFePO4 sudah mampu menunjukkan sifat sebagai baterai sekunder, berdasarkan adanya peak oksidasi dan reduksi pada voltamogram, serta berdasarkan pengujian charge/discharge. |
| Abtrak (Bhs. Inggris) | ABSTRACT Lithium Iron Phosphates (LiFePO4) glass cathodes are prepared using the melt quenching method at temperature of 900 oC with composition 5Li2O : 15 ZnO : x (Fe2O3) : (80-x) P2O5 where x = 0, 0,5, dan 1,5 (mol%). Thermal properties of the cathodes including glass transition temperature (Tg) and crystal temperature (Tc) are characterized using differential scanning calorimetry (DSC). Influence of Fe2O3 additions on structure and ionic conductivity of cathode are studied using X-Ray Diffraction and LCR meters, respectively. XRD diffraction pattern confirm that all of the cathode structure are armophous. The ionic conductivity of the cathode increase with increasing concentration of Fe2O3, but the conductivity tends to decrease up to 1,5% mol of Fe2O3. The highest ionic conductivity and capacity of the cathodes are 7,43 x 10-4 S/cm and 10 x 10-5 Ah/g respectively are exhibited by the glass cathode with 0,5% mol of Fe2O3. According to cyclic voltametry and charge/discharge tests, the obtained LiFePO4 glass are very potential to be used as cathode in secondary Li-battery. |
| Kata kunci | Kata Kunci: Baterai Ion Lithium, Katoda Kaca, LiFePO4, Konduktivitas Ionik |
| Pembimbing 1 | Dr. Ing Wahyu Widanarto |
| Pembimbing 2 | Dr. Eng Mukhtar Effendi |
| Pembimbing 3 | |
| Tahun | 2015 |
| Jumlah Halaman | 9 |
| Tgl. Entri | 2015-08-13 21:12:11.309454 |