| Judul Artikel | STRUKTUR DAN KONDUKTIVITAS IONIK KACA LiMnPO4 SEBAGAI KATODA PADA BATERAI SEKUNDER |
|---|
| Abstrak (Bhs. Indonesia) | Katoda kaca Lithium Manganese Phosphates (LiMnPO4) telah dibuat melalui reaksi solid state dan metode melt quenching pada temperatur 900 C dengan komposisi 5 Li2CO3 : x MnO2 : 15 ZnO : (80-x) P2O5 (dimana x = 0; 1,5 dan 3 dalam % mol). Karakterisasi sifat termal katoda yang meliputi temperatur transisi kaca Tg dilakukan dengan Differential Scanning Calorimetry (DSC). Pengaruh penambahan MnO2 terhadap struktur dan konduktivitas ionik katoda kaca dipelajari dengan menggunakan X-ray Diffraction (XRD) dan LCR meter. Pola difraksi XRD yang diperoleh menunjukkan bahwa struktur semua katoda adalah amorf. Konduktivitas ionik katoda meningkat dengan bertambahnya konsentrasi MnO2, namun konduktivitas cenderung menurun pada konsentrasi MnO2 yang berlebihan. Nilai konduktivitas ionik tertinggi katoda sebesar 7,25x10-4 S/cm ditunjukkan oleh katoda kaca yang mengandung 1,5% MnO2. Berdasarkan pengujian voltametri siklik dan charge/discharge, katoda kaca LiMnPO4 sangat berpotensi untuk digunakan dalam baterai Lithium sekunder. |
|---|
| Abtrak (Bhs. Inggris) | Glass Cathodes of Lithium Manganese Phosphates (LiMnPO4) are prepared using the melt quenching method at temperatures of 900 °C with composition 5 Li2CO3 : x MnO2 : 15 ZnO : (80-x) P2O5 (where x = 0, 1.5 and 3 mol %). Thermal properties of the cathodes including a glass transition temperature (Tg) iare characterized using Differential Scanning Calorimetry (DSC). Influence of the MnO2 addition on structure and ionic conductivity of cathodes are studied using X-ray Diffraction (XRD) and LCR meters. Respectively XRD diffraction patterns show that all of the cathode structures are amorphous. The ionic conductivity of the cathode increases with increasing of MnO2 concentration, but the conductivity tends to decrease at the excessive concentration of MnO2. The highest ionic conductivity of the cathode is 7.25x10-4 S/cm, exhibited by the glass cathode containing 1.5 mol % of MnO2. According to cyclic voltammetry and charge/discharge tests, the LiMnPO4 glass cathodes are very potential to be used in Secondary Lithium Battery. |
|---|
| Kata kunci | Baterai ion Lithium, Katoda Kaca, Lithium Manganese Phosphates, Konduktivitas Ionik, Baterai Sekunder |
|---|
| Pembimbing 1 | Dr,-Ing Wahyu Widanarto |
|---|
| Pembimbing 2 | Wahyu Tri Cahyanto, Ph.D |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 9 |
|---|
| Tgl. Entri | 2015-08-12 22:46:11.066869 |
|---|