| Judul Artikel | PEMBUATAN KACA KERAMIK LITHIUM PHOSPHATE DENGAN DOPING Fe2O3 ALAM SEBAGAI KATODA PADA BATERAI SEKUNDER |
|---|
| Abstrak (Bhs. Indonesia) | Baterai memiliki tiga komponen utama yaitu katoda, anoda dan elektrolit. Bahan katoda merupakan salah satu komponen kunci, untuk menunjang kinerja baterai, sehingga dibutuhkan penelitian intensif untuk fokus pada katoda. Katoda kaca keramik lithium phosphate dengan doping Fe2O3 telah dibuat menggunakan metode glass route pada temperatur 900 oC dengan komposisi 5 Li2CO3 : 15 ZnO : x Fe2O3 : (80 – x) P2O5 dimana x = 0; 0,5; 1,5 (dalam mol%). Stabilitas termal katoda kaca keramik ditelaah melalui penentuan temperatur kaca Tg dan temperatur kristal Tc. X-ray Diffraction dan LCR meter digunakan untuk menentukan fasa, struktur dan konduktivitas ionik katoda kaca keramik lithium phosphate dengan doping Fe2O3. Pola difraksi x-ray dari lithium phosphate dengan doping Fe2O3 menunjukkan fasa-fasa yang berbeda, LiFePO4 berhasil dibentuk pada penambahan 1,5% Fe2O3. Konduktivitas ionik meningkat seiring dengan bertambahnya konsentrasi doping Fe2O3. Nilai konduktivitas tertinggi yaitu 8,42 x 10-4 S/cm pada penambahan 1,5% Fe2O3, Analisa performa sampel dilakukan dengan melakukan uji voltametri siklik dan charge-discharge. Hasil uji menunjukkan bahwa katoda kaca keramik yang di buat, dimungkinkan dapat digunakan sebagai sel baterai namun kapasitas yang dimiliki sangat kecil jauh dari kapasitas teoritis katoda baterai sekunder Li-ion. |
|---|
| Abtrak (Bhs. Inggris) | The battery has there main components, cathode, anode, and electrolite. Cathode is one of important element to sustain the battery, so that we need an intensif research on catode. Ceramic-glass cathode of lithium phosphate with Fe2O3 as a dopping has been made using glass route method at 900 oC with the composition 5 Li2CO3 : 15 ZnO : x Fe2O3 : (80 – x) P2O5¬ where x = 0. 0,5. 1,5 (in mol percent). Ceramic-glass cathode thermal stability is studied through determination of glass temperature Tg and crystal temperature Tc. X-ray diffraction and LCR meter are used to determine phase, structure and ionic conductivity of lithium phosphate with Fe2O3 ceramic-glass cathode. X-ray diffraction pattern of lithium phosphate with Fe2O3 dopping shows different phases, and LiFePO4 is formed at 1.5% addition of Fe2O3. Ionic conductivity rise up by the increase of Fe2O3 concentration, the highest conductivity is 8,42 x 10-4 S/cm at 1.5% addition of Fe2O3. Sample performance analyzing is done by cyclic voltammetry and charge-discharge test. The result shows that well-made ceramic-glass cathode can be used as battery, despite of a very wide gap of Li-ion battery capacity result in experiment and theory. |
|---|
| Kata kunci | Kata Kunci : Kaca keramik, Katoda baterai, lithium phosphate, konduktivitas. |
|---|
| Pembimbing 1 | Dr.Ing Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr. Eng Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 9 |
|---|
| Tgl. Entri | 2015-08-12 14:28:41.37963 |
|---|