| NIM | H1A010018 |
|---|
| Namamhs | PUPUT ANGGRAENI |
|---|
| Judul Artikel | KARAKTERISASI MEMBRAN KOMPOSIT SELULOSA ASETAT (SA) DARI NATA DE CASSAVA-POLIETILEN GLIKOL (PEG) DENGAN VARIASI PENAMBAHAN POLISTIRENA (PS) |
|---|
| Abstrak (Bhs. Indonesia) | Pemanfaatan limbah cair tapioka sebagai alternatif pembuatan membran selulosa asetat (SA) dari nata de cassava yang memiliki nilai ekonomis serta memberi solusi alternatif menanggulangi pencemaran lingkungan perairan. Membran SA memiliki sifat mekanik yang rendah sehingga dilakukan penambahan aditif dengan variasi polistirena (PS) dan polietilen glikol (PEG). Penelitian ini bertujuan untuk mengetahui karateristik SA berdasarkan fluks dan uji tarik membran. Berdasarkan hasil penelitian nata de cassava berwarna putih dan kenyal. Selulosa asetat diperoleh melalui proses asetilasi. SA berwarna coklat kekuningan sebagai bahan dasar pembuatan membran. Karakterisasi membran dilakukan dengan analisis kadar asetil diperoleh 36,5585%, penentuan bobot molekul relatif (Mv) sebesar 4,68 x 10-4 g/mol dan analisis FTIR menunjukkan adanya serapan gugus (C=O karbonil) 1739.83 cm-1 serta terjadi penyerapan (C-O) 1233,26 cm-1. Metode yang digunakan untuk pembuatan membran komposit SA-PS-PEG yaitu inversi fasa. Karakterisasi membran komposit dilakukan dengan uji fluks air dan uji tarik membran. Hasil pengukuran diperoleh nilai fluks air terbesar yaitu membran komposit 1 sebesar 0,9 L/(m2.Jam) dan modulus young terbesar sebesar 1,1949 MPa untuk membran komposit 3. |
|---|
| Abtrak (Bhs. Inggris) | Utilization tapioca liquid waste as an alternative to the manufacture cellulose acetate membrane (SA) of nata de cassava, that has economic value and provide alternative solutions to tackle pollution of aquatic environment. Membrane SA has a low mechanical properties, it needs polystyrene (PS) and PEG as additives. This study goals to determine characteristics of SA based on flux and tensile membrane. Based on the results, nata de cassava are white and chewy. Cellulose acetate is obtained by acetylation. SA has a yellowish brown color. It is a raw materials for manufacturing of membranes. Membrane characterization performed by 36.5585% of acetyl content, the determination of the relative molecular weight (Mv) of 4.68 x 10-4 g/mol and FTIR analysis showed uptake group (C=O carbonyl) 1739.83 cm-1 and the absorption (C-O) 1233.26 cm-1. The method used for the manufacturing of composite membranes SA-PS-PEG is phase inversion. Characterization of composite membranes made with test water flux and tensile membrane. The measurement results obtained value that the largest water flux is composite membrane 1 of 0,9 L /(m2.h) and most young modulus of 1.1949 MPa for composite membrane 3. |
|---|
| Kata kunci | limbah cair tapioka, nata de cassava, selulosa asetat (SA), polistirena (PS), karakterisasi membran komposit |
|---|
| Pembimbing 1 | Senny Widyaningsih, S.Si, M.Si |
|---|
| Pembimbing 2 | Dr Ponco Iswanto, S.Si, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | 2015-07-30 21:20:22.851585 |
|---|