| Judul Artikel | PENGARUH LAMA PERENDAMAN DALAM LARUTAN PEMBERSIH GIGI TIRUAN TERHADAP MODULUS ELASTISITAS DAN KARAKTERISTIK MIKROSTRUKTUR TISSUE CONDITIONER |
|---|
| Abstrak (Bhs. Indonesia) | Tissue conditioner merupakan suatu bahan pelapis yang berfungsi sebagai bantalan namun memiliki kekurangan yaitu sifat absorbsi yang tinggi. Pembersihan secara kimia dianjurkan untuk membersihkan tissue conditioner. Kandungan ion yang tinggi (natrium dan kalium) yang ada pada larutan pembersih gigi tiruan mempercepat hilangnya kandungan plasticizer pada tissue conditioner. Tujuan penelitian ini adalah mendeskripsikan dan membandingkan modulus elastisitas (ME) dan karakteristik mikrostruktur (EDS) tissue conditioner dengan lamanya waktu perendaman dalam larutan pembersih gigi tiruan yang berbeda. Sampel tissue conditioner dibuat sebanyak 25 sampel. Sampel dibagi menjadi 5 kelompok dengan kelompok A sebagai kelompok kontrol, kelompok B sampel direndam dalam larutan pembersih gigi tiruan selama 1 minggu, kelompok C selama 4 minggu, kelompok D selama 5 minggu, dan kelompok E selama 6 minggu. Masing-masing kelompok direndam selama 15 menit perhari. Modulus elastisitas di uji dengan menggunakan Universal Testing Machine (UTM) dan karakteristik mikrostruktur dengan Energy Dispersive Spectroscopy (EDS). Hasil rata-rata ME (kelompok A: 165,43 kPa, B: 521,53 kPa, C: 675,39 kPa, D: 790,86 kPa, dan E: 885,68 kPa) dan EDS (kelompok A: (-), B: Na (0,06%), C: Na (0,09%), D: Na (0,11%), dan E: Na (0,18%). Nilai ME meningkat seiring dengan lama perendaman dalam larutan pembersih gigi tiruan, hal ini disebabkan oleh sifat absorbsi dan porositas bahan yang tinggi. Kandungan natrium (Na) yang terdeteksi pada EDS membuktikan bahwa natrium menggantikan kandungan plasticizer. Tissue conditioner akan semakin kehilangan elastisitasnya seiring dengan lama perendaman dalam larutan pembersih gigi tiruan. |
|---|
| Abtrak (Bhs. Inggris) | Tissue conditioner is a lining that serves as a cushion but it has the disadvantage that the high absorption properties. Chemical cleaning is recommended to clean the denture base with tissue conditioner. High content of ions (sodium and potassium) that exist on denture cleaning solution accelerates the loss of plasticizer content of the tissue conditioner. The purpose of this study was to describe and compare the modulus elasticity (ME) and microstructure characteristics (EDS) tissue conditioner with the different time of soaking in a solution of denture cleaners. 25 samples of tissue conditioners was made and the samples were divided into 5 groups, group A as a control group, group B which the samples were soak in a denture cleaning solution for 1 week, group C for 4 weeks, group D for 5 weeks, and group E for 6 weeks. Each group was soaked for 15 minutes each day. Modulus elasticity test by using a Universal Testing Machine (UTM) and microstructure characteristics with Energy Dispersive Spectroscopy (EDS). Average result of ME (group A: 165.43 kPa, B: 521.53 kPa, C: 675.39 kPa, D: 790.86 kPa, and E: 885.68 kPa) and EDS (group A: ( -), B: Na (0.06%), C: Na (0.09%), D: Na (0.11%), and E: Na (0.18% ). ME value increases with length of immersion in a denture cleaning solution, this is caused by the high absorption and high porosity of the materials. The content of sodium (Na) were detected at EDS and proving that the sodium is replacing the content of plasticizer in tissue conditioner. Tissue conditioner will increasingly lose elasticity as long immersion in a denture cleaning solution. |
|---|
| Kata kunci | Tissue Conditioner, Modulus Elastisitas, Karakteristik Mikrostruktur, Energy Dispersive Spectroscopy (EDS) |
|---|
| Pembimbing 1 | drg. Setiadi W. Logamarta, Sp. Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M. Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2015-06-26 13:14:26.167868 |
|---|