| Judul Artikel | PENGARUH PENAMBAHAN GLASS FIBERS 1% TERHADAP PENYERAPAN AIR DAN KEKUATAN TRANSVERSA BASIS GIGITIRUAN NILON TERMOPLASTIK DERAJAT KRISTALIN TINGGI
|
|---|
| Abstrak (Bhs. Indonesia) | Perendaman gigitiruan dalam jangka waktu tertentu dapat menyebabkan penyerapan air sehingga kekuatan bahan basis gigitiruan menurun. Penambahan glass fibers 1% dalam bahan basis gigitiruan dapat menurunkan penyerapan air serta meningkatkan kekuatan transversa. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan glass fibers 1% terhadap penyerapan air dan kekuatan transversa basis gigitiruan nilon termoplastik derajat kristalin tinggi. Jenis penelitian ini adalah eksperimental dengan menggunakan 34 sampel nilon termoplastik derajat kristalin tinggi yang dibagi secara acak menjadi dua kelompok dengan masing-masing kelompok terdiri dari 17 sampel. Kelompok kontrol tidak diberikan penambahan glass fibers, sedangkan kelompok perlakuan diberikan penambahan glass fibers 1% (w/w). Setiap kelompok direndam dalam aquades selama 10 hari dan disimpan dalam inkubator dengan suhu 370 C. Uji penyerapan air dilakukan dengan neraca digital dan uji kekuatan transversa dilakukan dengan alat Torsee’s Electronic System Universal Testing Machine. Uji Independent T-Test menunjukkan adanya perbedaan yang bermakna pada besar penyerapan air dan kekuatan transversa antara kedua kelompok dengan p = 0,000 (p < 0,005). Kelompok perlakuan memiliki nilai penyerapan air yang lebih rendah (14,22 μg/mm3) dibandingkan dengan kelompok kontrol (20,91 μg/mm3). Kelompok perlakuan juga memiliki nilai kekuatan transversa yang lebih tinggi (93,62 MPa) dibandingkan dengan kelompok kontrol (67,99 MPa). Penambahan glass fibers 1% (w/w) terhadap bahan basis gigitiruan nilon termoplastik derajat kristalin tinggi dapat menurunkan besar penyerapan air dan meningkatkan kekuatan transversa. |
|---|
| Abtrak (Bhs. Inggris) | Water immersion in certain time can cause water absorption and change in strength material of denture base. 1% glass fibers reinforcement can decrease water absorption and increase flexural strength of denture base. This research is aimed to determine the effect of 1% glass fibers reinforcement on water absorption and flexural strength of high crystalline degree nylon thermoplastic denture base. This study was an experimental laboratory research using 34 samples of high crystalline degree nylon thermoplastic denture base that were randomly divided into 2 groups: treatment group (reinforced by 1% w/w glass fibers) and control group (without any treatment) in which each of them consisted of 17 samples. Each sample was immersed in distilled water for 10 days and stored in an incubator that the temperature was 370C. Water absorption test was conducted by using an analytical scale, while flexural strength test was determined with Torsee’s Electronic System Universal Testing Machine. Independent T-Test revealed that there were statistically significant differences on water absorption and flexural strength between the treatment and control group p=0,000 (p<0,005). The water absorption value of the treatment group (14,22 μg/mm3) was lower than that of the control group (20,91 μg/mm3). The flexural strength value of the treatment group (93,62 MPa) was higher than that of the control group (67,99 MPa). The reinforcement of 1% (w/w) glass fibers could decrease the water absorption and increase the flexural strength of high crystalline degree nylon thermoplastic denture base. |
|---|
| Kata kunci | Glass fibers, nilon termoplastik, penyerapan air, kekuatan transversa |
|---|
| Pembimbing 1 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 2 | drg. Setiadi W. Logamarta, Sp. Ort |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 18 |
|---|
| Tgl. Entri | 2015-06-15 20:37:51.023354 |
|---|