| NIM | G1G010039 |
|---|
| Namamhs | NOVITA DWI SAPUTRI |
|---|
| Judul Artikel | PENGARUH COUPLING AGENT KITOSAN 2%, 4% DAN 6% TERHADAP MIKROSTRUKTUR DAN NILAI KEKERASAN KOMPOSIT ALUMINA ZIRKONIA - KARBONAT APATIT SEBAGAI MATERIAL RESTORASI GIGI DIRECT |
|---|
| Abstrak (Bhs. Indonesia) | Komposit merupakan salah satu material restorasi direk kedokteran gigi yang terbentuk oleh tiga komponen utama yaitu matriks, filler dan coupling agent. Bahan yang berasal dari alam seperti alumina, zirkonia, karbonat apatit dan kitosan mulai dikembangkan sebagai material restorasi gigi. Dalam penelitian ini, komposit sebagai restorasi direk gigi dibuat dengan cara mencampur alumina zirkonia-karbonat apatit sebagai filler, UDMA-TEGDMA-DMAEMA-HEMA sebagai matrik dengan penambahan kitosan sebagai coupling agent. Rasio filler dan matriks yang digunakan adalah 70:30. Pengaruh berbagai macam variasi konsentrasi kitosan sebagai coupling agent (2%,4%,6%) kemudian dievaluasi dari mikrostruktur dan kekerasan komposit. Sampel dibuat dengan melakukan sintesis untuk menghasilkan filler alumina-zirkonia dan filler karbonat apatit. Sampel dibagi menjadi tiga kelompok dengan penambahan masing-masing coupling agent kitosan 2% (sampel A), kitosan 4% (sampel B) dan kitosan 6% (sampel C). Hasil SEM menunjukkan ukuran partikel sampel A: 87,5 nm; B: 112,5 nm; C: 150 nm. Hasil uji kekerasan sampel A: 43,2 VHN; B: 26,47 VHN; C: 25,84 VHN. Kesimpulan dari penelitian ini adalah semakin rendah konsentrasi kitosan yang digunakan, semakin tinggi nilai kekerasan komposit dan semakin baik distribusi partikel yang diperoleh.
|
|---|
| Abtrak (Bhs. Inggris) | Composite, one of direct restoration components in dentistry, is generally consist of three primary ingredients: matrix, filler, and coupling agent. Ingredients derived from nature such as alumina, zirconia, carbonate apatite and chitosan are recently developed as dental restoration material. In this work, composite for direct restration was prepared by mixing alumina zirconia-carbonate apatite as filler with UDMA-TEGDMA-DMAEMA-HEMA as matrix in the presence of chitosan as coupling agent. Weight ratio filler to matrix used was 70:30. The effect of various concentration of chitosan coupling agent (2%,4%,6%) was then evaluated towards composite microstructure and hardness. Sample prepared by synthetizing process to obtain alumina-zirconia filler and carbonat apatite filler. The sample were divided into three groups according to the amount of coupling agent added: Group A (2% chitosan), Group B (4% chitosan), Group C (6% chitosan). SEM images revealed that the particle size of each sample was 87,5 nm (Group A), 112,5 nm (Group B), and 150 nm (Group C). The hardness values of each sample is 43,2 VHN (Group A), 26,47 VHN (Group B), and 25,84 VHN (Group C). As conclusion, the lower concentration of chitosan, the higher hardness value of the composite, and the better particle distribution of composite were obtained.
|
|---|
| Kata kunci | Coupling agent, kitosan, komposit, alumina-zirkonia-karbonat apatit, mikrostruktur, kekerasan. |
|---|
| Pembimbing 1 | Prof. Dr. Ir. Bambang Sunendar P. M. Eng |
|---|
| Pembimbing 2 | Dr. drg. A. Haris Budi W., M. Kes., AP., S. IP. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2015-05-25 21:19:22.166953 |
|---|