| Judul Artikel | PENGARUH KEKASARAN PASIR TERHADAP SUSUT BETON NORMAL |
| Abstrak (Bhs. Indonesia) | Kerusakan pada beton bukan hanya diakibatkan karena pembebanan yang ditumpu pada beton namun dapat berasal dari beban beton itu sendiri, jika beton mengalami susut dan rangkak yang berlebih maka beton akan mengalami retak. Penelitian ini bertujuan untuk mengetahui penyusutan pada beton normal dengan variasi gradasi agregat halus yaitu pasir kasar (golongan 1), pasir agak kasar (golongan 2), pasir agak halus (golongan 3), pasir halus (golongan 4). Setelah mendapatkan data dari hasil penelitian di laboratorium, penyusutan yang terjadi akan dibandingkan dengan suatu metode perhitungan yaitu metode ACI 209R-92 Pengujian terdiri dari uji material, kuat tekan beton dan uji susut. Uji kuat tekan beton dilakukan pada umur 28 hari dengan kuat tekan rencana fc’ 27 MPa dan uji susut dilakukan selama 28 hari. Untuk kuat tekan beton benda uji dibuat silinder berdiameter 15cm dan tinggi 30cm, sementara itu benda uji susut berukuran balok 7,5cm x 7,5cm x 25cm (Standar ASTM C490-04). Hasil penelitian menunjukkan persentase susut terkecil pada sampel variasi golongan 1 sebesar 0,056%, persentase terbesar pada sampel variasi golongan 3 sebesar 0,096%. Setelah dibandingkan dengan metode ACI 209R-92, pengujian susut yang dilakukan di laboratorium memiliki nilai susut yang lebih besar dibandingkan dengan perhitungan, selisih yang terjadi cukup besar, selisih paling kecil terjadi pada sampel variasi gradasi pasir golongan 1 sebesar 0,000385 mm. Selisih yang terjadi dapat disebabkan oleh proses pembuatan beton, perawatan beton, suhu ruangan yang berubah-ubah, getaran yang terjadi disekitar tempat praktikum. |
| Abtrak (Bhs. Inggris) | Damage of concrete is not only caused by loading on concrete but can be derived from the concrete load itself. If the shringkage and creep of concrete experiencing excessive, then it would have cracked. Shringkage research that has been done is to use additional fiber or high strength concrete. The aims of this study was to determine on normal concrete with fine aggregate gradation variation are coarse sand (class 1), sand rather coarse (class 2), rather find sand (class 3), soft sand (class 4). After getting data from research in laboratory, the shringkage on concrete will be compared with a calculation method, the method from ACI 209R-92. The test consist of test material, concrete compressive strength and shringkage test. Concrete compressive strength test performed at 28 days with a plan of compressive strength f’c 27 MPa and shringkage test performed at 28 days. Concrete compressive strength test specimen were made cylinder with diameter 15 cm and a height 30 cm. While the shringkage specimen beam shaped 7,5 cm x 7,5 cm x 25 cm (ASTM standard C490-04) Results of laboratory studies showed the smallest percentage of shringkage in the sample variation class 1 as big as 0,056 %, the largest percentage sample variation in class 3 in as big as 0,096 %. After compared with ACI method 209R-92, shringkage test conducted in the laboratory have bigger shringkage value than the calculation, the smallest difference occurs in the sample of gradation variation sand class 1 as big as 0,000385 mm the differences is quite huge. Differences may occur due to the process of making concrete, concrete treatment, room temperature changing, and vibrations that occur around the laboratory. |
| Kata kunci | Kata kunci : Susut Beton Normal, Gradasi Agregat Halus, Metode ACI 209R-92 |
| Pembimbing 1 | Gandjar Pamudji,.S.T,.MT. |
| Pembimbing 2 | Gathot Heri Sudibyo,.S.T,.MT. |
| Pembimbing 3 | |
| Tahun | 2015 |
| Jumlah Halaman | 13 |
| Tgl. Entri | 2015-02-19 10:48:58.30634 |