| Judul Artikel | PERBANDINGAN BESAR KEKUATAN GESER BONDING KOMPOSIT BREKET MENGGUNAKAN PHOSPORIC ACID 37% DAN HYDROFLUORIC ACID 9,6% DENGAN PENAMBAHAN SILANE PADA PERMUKAAN PORSELEN |
|---|
| Abstrak (Bhs. Indonesia) | Permukaan porselen yang halus menyebabkan sulitnya penetrasi bahan adesif pada pasien yang sedang dilakukan perawatan ortodontik, sehingga menyebabkan kurangnya retensi yang didapat. Penambahan silane sebagai coupling agent dapat meningkatkan retensi antara bahan adesif dengan permukaan porselen. Penelitian ini bertujuan untuk membandingkan kekuatan geser bonding komposit breket menggunakan phosporic acid 37% dan hydrofluoric acid 9,6% dengan penambahan silane serta hydrofluoric acid 9,6% tanpa penambahan silane pada permukaan porselen. Jenis penelitian ini adalah eksperimen laboratorium murni dengan metode post test control group design. Sebanyak 27 sampel porcelain fused to metal (PFM) insisivus pertama rahang atas dibagi secara acak menjadi tiga kekompok dengan masing-masing kelompok terdiri dari 7 PFM. Bahan adesif yang digunakan berupa self cure adesif bonding. Breket yang digunakan adalah standard edgewise untuk insisivus pertama rahang atas dengan permukaan mesh base. Kelompok 1 pengaplikasian hydrofluoric acid 9,6% tanpa silane, kelompok 2 pengaplikasian hydrofluoric acid 9,6% dengan silane, dan kelompok 3 pengaplikasian phosporic acid 37% dengan silane. Uji kekuatan geser dilakukan dengan alat Pearson Panke Equipment Universal Testing Machine. Uji ANOVA menunjukkan adanya perbedaan yang bermakna antara ketiga kelompok dengan p=0,000 (p<0,05). Kelompok 2 memiliki nilai kekuatan geser tertinggi (4,72 MPa), selanjutnya kelompok 3 (3,79 MPa), dan kelompok 1 (1,76 MPa). Kelompok 1 berbeda secara signifikan (p<0,05) dengan kelompok 2 dengan p=0,000 dan kelompok 3 dengan p=0,001, sedangkan kelompok 2 dengan 3 tidak berbeda secara signifikan dengan p=0,395. Bahan adesif dengan penambahan silane pada permukaan porselen menghasilkan kekuatan yang lebih tinggi dibandingkan dengan bahan adesif tanpa penambahan silane. Saran yang dapat diberikan adalah penggunaan rubber dam dan sarung tangan pada saat pengaplikasian hydroflouric acid dapat meminimalisir sifat toksik dan iritatif terhadap mukosa. |
|---|
| Abtrak (Bhs. Inggris) | Porcelain that have smooth surface which causes difficulty in penetration of the adhesive material who sometimes are in orthodontic treatment. In order to increase the retention a material can be added such as silane coupling agent as copolymers between adhesive material and porcelain surface. The aim of this research was to compare the shear bond strength of composite brackets which used phosporic acid 37% and hydrofluoric acid 9,6% added by silane and hydrofluoric acid 9,6% without silane on porcelain surface. The type of this study was laboratory experiment with post test control group design method. A total 27 samples of porcelain fused to metal (PFM) maxilla first incisor divided by 3 groups randomly there were 7 PFM in each group. The adhesive material were used self cure adhesive bonding. The bracket were used standart edgewise for the maxilla first incisor with mesh base surface. The application of group 1 were etched with 9,6% hydrofluoric acid without silane, group 2 were etched with 9,6% hydrofluoric acid followed by silane, and group 3 were etched with 37% phosporic acid followed by silane. The pearson panke equipment universal testing machine was used to test the shear bond strength. The results of the analysis ANOVA indicated that there was a significant difference between the three groups with p=0,000 (p<0,05). The group 2 indicated the highest shear bond strength 4, 72 MPa, the group 3 indicated 3,79 MPa, and the group 1 indicated the lowest shear bond strength 1,76 MPa. The group 1 had significant difference (p<0,05) between group 2 with p=0,000 and group 3 with p=0,001, while group 2 and group 3 hadn’t significant difference with p=0,395. Adhesive material with silane on porcelain surface create highest strength compare with adhesive material without silane. For the suggestion on this research is use the rubber dam and gloves when aplication hydroflouric acid can minimize the toxic and iritative effect towards mucosa. |
|---|
| Kata kunci | hydroflouric acid, phosporic acid, silane, porselen, uji geser |
|---|
| Pembimbing 1 | drg. Setiadi W. Logamarta, Sp.Ort |
|---|
| Pembimbing 2 | drg. Rinawati Satrio, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2015 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2015-02-18 14:19:10.793972 |
|---|