KHOIRUN NIDA NUR
NIM
Judul Artikel
Kajian Termodinamika dan Kinetika Adsorpsi Modifikasi Kitosan Magnetit dan SiO2 pada Zat Warna Malachite Green
Abstrak (Bhs. Indonesia)
Industri di Indonesia mengalami peningkatan produksi limbah seiring perkembangan zaman, salah satunya yaitu limbah cair dari proses pewarnaan. Malachite green (MG) adalah salah satu zat warna yang sering digunakan, namun memiliki kandungan senyawa yang bersifat toksik, sehingga dapat berdampak terhadap kesehatan. Salah satu metode yang telah dikembangkan untuk pengolahan limbah cair yaitu metode adsorpsi. Penelitian ini dilakukan untuk mengetahui karakteristik SiO2 dan Fe3O4@SiO2-CS, studi termodinamika, studi adsorpsi, energi aktivasi, serta pengujian pemakaian berulang Fe3O4@SiO2-CS. Senyawa SiO2 dihasilkan dari abu layang dengan metode sol gel yang berupa padatan kasar berwarna putih dan hasil sintesis Fe3O4@SiO2-CS berupa padatan berwarna hitam yang dapat ditarik menggunakan batang magnet. Hasil karakterisasi FTIR, XRD, SEM-EDX, BET, VSM menunjukkan adanya serapan –NH, Fe–O, dan Si–O–Si, struktur kubik Fe3O4, perubahan morfologi dan ukuran partikel, serta sifat kemagnetan dari Fe3O4@SiO2-CS. Analisis pH PZC diperoleh pada pH 5. Studi termodinamika menunjukkan proses adsorpsi berlangsung secara endotermik dan spontan. Adsorpsi MG mengikuti kinetika PSO dan Isoterm Freundlich dengan energi aktivasi sebesar 28,248 kJ/mol. Uji reusability menunjukkan efisiensi adsorben Fe3O4@SiO2-CS setelah lima kali pemakaian ulang. Hasil ini menunjukkan bahwa Fe3O4@SiO2-CS merupakan adsorben potensial dan ramah lingkungan dalam mengatasi pencemaran zat warna MG di limbah industri.
Abtrak (Bhs. Inggris)
The industry in Indonesia is experiencing an increase in waste production along with the times, one of which is liquid waste from the dyeing process. Malachite green (MG) is one of the dyes that is often used, but it contains toxic compounds that can impact health. One method that has been developed for the treatment of liquid waste is the adsorption method. This research was conducted to understand the characteristics of SiO2 and Fe3O4@SiO2-CS, thermodynamic studies, adsorption studies, activation energy, and testing the repeated use of Fe3O4@SiO2-CS. The SiO2 compound was produced from fly ash using the sol-gel method, resulting in a coarse white solid, while the synthesis of Fe3O4@SiO2-CS produces a black solid that can be attracted by a magnet. The characterization resultsed from FTIR, XRD, SEM-EDX, BET, and VSM show the presence of –NH, Fe–O, and Si–O–Si absorption, the cubic structure of Fe3O4, changes in morphology and particle size, as well as the magnetic properties of Fe3O4@SiO2- CS. The PZC pH analysis obtained at pH 5. Thermodynamic studies indicated that the adsorption process occurs endothermically and spontaneously. Adsorption of MG follows PSO kinetics and Freundlich isotherm with an activation energy of 28.248 kJ/mol. Reusability tests demonstrated the efficiency of the Fe3O4@SiO2-CS adsorbent after five reuse cycles. These results showed that Fe3O4@SiO2-CS is a potential and environmentally friendly adsorbent in addressing the pollution of the dye MG in industrial waste.
Kata kunci