SINTESIS CARBON QUANTUM DOTS TERDOPING NITROGEN SULFUR (NSCQDs) SEBAGAI KO-KATALIS BISMUT VANADAT (BiVO4) PENDEGRADASI METILEN BIRU
Abstrak (Bhs. Indonesia)
Degradasi metilen biru (MB) dilakukan dengan metode fotokatalisis menggunakan material komposit BiVO4/NSCQDs dengan sinar visibel sebagai sumber energi. Penelitian ini mengkaji karakteristik dan aktivitas fotokatalitik melalui variasi volume NSCQDs, waktu degradasi, serta pH metilen biru. Selain itu, laju kinetika reaksi dan mekanisme degradasi fotokatalitik juga dianalisis. Karakterisasi material dilakukan menggunakan teknik XRD, SEM-EDX, TEM,BET dan UV-Vis DRS. Hasil yang diperoleh menunjukkan bahwa komposit BiVO4/NSCQDs dengan penambahan 1,5 mL NSCQDs pada pH 9 dengan waktu degradasi 150 menit mampu mendegradasi metilen biru hingga 98,6 %. Laju kinetika fotokatalitik mengikuti orde satu dengan radikal superoksida (•O2-¬) sebagai spesies utama dalam mekanisme degradasi. Struktur kristal BiVO4 terdoping NSCQDs memiliki fase ortorombik dengan ukuran kristal 9,10 nm, morfologi spehere like grape, ukuran rata-rata NSCQDs yang terbentuk sebesar 7,03 nm, dengan luas permukaan 14,96 m2/g dan energi celah pita sebesar 2,49 eV.
Abtrak (Bhs. Inggris)
The degradation of methylene blue (MB) was analyzed using the photocatalysis method with BiVO4/NSCQDs composite material and visible light as the energy source. This research investigates the characteristics and photocatalytic activity of the composite by varying the volume of NSCQDs, degradation time, and the pH of methylen blue. Additionally, the reaction kinetics and the photocatalytic degradation mechanism were analyzed. Material characterization was performed using XRD, SEM-EDX, TEM, BET and UV-Vis DRS technique. The result show that the BiVO/NSCQDs composite with addition of 1.5 mL of NSCQDs at pH 9 and a degradation time of 150 minutes achieved a methylene blue degradation efficiency of up to 98,6 %. The photocatalytic reaction kinetics adhere to pseudo first order, with superoxide radical (•O2-¬) as the main active species in the degradation mechanism. The crystal structure of NSCQDs-doped BiVO4 exhibits an orthorombic phase, with a crystal size of 9.10 nm, a sphere like grape morphology,the average size of the NSCQDs formed is equal 7,03 nm with the surface area 14,96 m2/g and a band gap energy of 2.49 eV.
Kata kunci
Pembimbing 1
Pembimbing 2
Pembimbing 3
Tahun
Jumlah Halaman
Save