Sintesis dan karakterisasi reduced graphene oxide (rGO) berbahan dasar arang aktif sekam padi sebagai elektroda superkapasitor telah berhasil dilakukan. Raw material arang aktif sekam padi dibuat melalui proses karbonisasi menggunakan Muffle Furnace PPF-UG pada suhu 300 ℃ selama 1 jam dan proses aktivasi dengan KOH 50% selama 24 jam perendaman. Selanjutnya, dilakukan sintesis rGO berbahan dasar arang aktif sekam padi dengan menggunakan metode mechanical milling selama 50 menit dan reduksi termal menggunakan furnace pada suhu 200 ℃ selama 30 menit. Kemudian rGO tanpa proses reduksi termal telah diamati untuk melihat pengaruh dari reduksi termal. Sampel kemudian dikarakterisasi menggunakan X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), Energy Dispersive X-Ray (EDX) dan Surface Area Analyzer (SAA). Hasil karakterisasi menunjukkan adanya pengaruh reduksi termal terhadap struktur, morfologi, dan luas permukaan rGO. Karakterisasi dengan metode BET mengungkapkan bahwa sampel setelah diberikan pemanasan menunjukan luas permukaan yang meningkat dan diameter pori kecil yang menguntungkan untuk aplikasi elektroda pada superkapasitor. Luas permukaan dan diameter pori yang dihasilkan secara berurut sebesar 121,244 m2/g dan 4,893 nm, Hasil penelitian ini berpotensi memberikan kontribusi dalam pengembangan elektroda superkapasitor berbasis rGO yang lebih efisien dan berkelanjutan.

Abtrak (Bhs. Inggris)

Synthesis and characterization of reduced graphene oxide (rGO) based on activated charcoal from rice husk as a supercapacitor electrode has been successfully carried out. Active rice husk charcoal raw material was made through a carbonization process using Muffle Furnace PPF-UG at 300 ℃ for 1 hour and activation process with 50% KOH for 24 hours soaking. Furthermore, the synthesis of rGO made from active charcoal from rice husk was carried out using the mechanical milling method for 50 minutes and thermal reduction using a furnace at 200 ℃ for 30 minutes. Then rGO without thermal reduction process was observed to see the effect of thermal reduction. The samples were then characterized using X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), Energy Dispersive X-Ray (EDX) and Surface Area Analyzer (SAA). The characterization results showed that there was an effect of thermal reduction on the structure, morphology, and surface area of rGO. Characterization by the BET method revealed that the sample after being given heating showed an increased surface area and small pore diameter which is advantageous for electrode applications in supercapacitors. The resulting surface area and pore diameter are 121.244 m2/g and 4.893 nm respectively. The results of this study have the potential to contribute to the development of more efficient and sustainable rGO-based supercapacitor electrodes.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman